Calculated Hardenability And Weldability Of Carbon And Low-Alloy Steels

THE relationship between hardenability and weldability has been mentioned many times. The ease of making a hardness survey has led to its wide use as a criterion [ ] of weldability and with a given class or series of steels for which the ductility under weld heat-treatment is known the test is entirely suitable. However, in studying a new steel the hardness survey is of less value, since it is based on the assumption that there is a correlation between hardness and ductility. Several attempts have been made to derive indices for weldabilityl and hardenability from the chemical analysis. In most of these proposals the effects of the different elements were considered to be additive, but recently Grossmami2 proposed a novel method of calculating the hardenability of a steel from its chemical composition. In the [ ] method proposed, a steel is considered as having a base hardenability due to its carbon content and grain size, and this base hardenability is multiplied by a factor for each chemical element present, The final product is the hardenability. The purpose of the present study is to point out the possible relationship between hardenability and the effect of welding on hardness and ductility for a number of plain carbon and low-alloy steels. The composition of the 25 steels reported in this paper as determined by chemical analysis is given in Table I. To eliminate the effect of variations in finishing temperatures, the 1/2-in. plates were normalized after heating for one hour at 1650°F. in a controlled-atmosphere furnace.