Cooling innovation in practice: A case study on composite copper-graphite cooler performance before and after a PGM furnace partial sidewall rebuild

Sibanye-Stillwater recently completed a partial sidewall rebuild on Furnace 1 at its Marikana smelter complex. The project involved matte taphole maintenance, which required the removal and subsequent replacement of 18 composite copper-graphite coolers and a section of the lower refractory sidewall. These composite copper-graphite coolers are a newly developed cooling design by Tenova Pyromet, and this rebuild project provided valuable insight into the performance of the composite coolers. The novel composite cooler design was implemented to serve as a safeguard against localised wear and corrosion in the furnace sidewall, particularly at the slag-concentrate interface, where chloride-accelerated sulphidation has been identified as a dominant degradation mechanism affecting the copper cooling elements. The composite cooler design is unique in that all the exposed sides of the water-cooled copper elements are fully encapsulated in graphite, which protects the copper from corrosive sulphur- and chlorinebearing gases and condensates. This sidewall cooling system was designed to improve corrosion resistance, stabilise freeze lining formation, and extend the campaign life of the furnace sidewall. The partial sidewall rebuild was executed during a planned maintenance shutdown with the main objective of replacing the matte taphole lintel bricks. This paper serves as a case study that compares and evaluates the operational performance of the composite coolers before and after the rebuild. The installation method is discussed to highlight the approach taken to ensure a sound installation while minimising downtime, as well as to present some lessons learned in the process.