Copper-Based Multi-Component Alloys by Vacuum Distillation to Separate Copper Enriched Lead , Silver And Other Valuable Metals Research

"In this paper, vacuum distillation technology has been employed to study the possibility and regularity of separating copper and enriching lead, silver and other valuable metals from copper- based multi component alloys. The result of experiment indicated the practicability of vacuum distillation dealing with copper base complex multi-component alloy to separating lead and silver, when the vacuum distillation temperature was 1637K, distillation time was 60min; residual gas pressure was 20-30Pa, the removal rate of silver was 95.86%, of lead was 99.63%; the evaporation rate of copper was 0.745%. The removal rate of arsenic, antimony and tin respectively were 83.09%, 48.12% and 24.54%. Vacuum distillation method is applicable for dealing with the copper-based multi component alloys, silver and lead can realize effective recovery.IntroductionCopper generally go with lead mineral, therefore, to remove copper from lead becomes an inevitable link in lead smelting. Dross from removed copper usually contains lead, arsenic, antimony, tin and noble metal silver. In abroad, soda ash-iron dust is adopted to process copper dross of this kind. The outcomes of this process are lead matte, wet lead, scoria smoke dust etc[1~5] The dominant components of all the outcomes are copper and lead. Moreover, in the process of tin smelting, copper contained by-products are produced, such as, crude tin alloy, tin lead electrolytic anode slime and so on. Copper content of all the products are ranging from few percentages to several tens percentage. Those products, no matter merge into main producing process, or separate treatment cost losses of valuable metal. For one hand, the containing of copper of outcomes from pyrogenic attack is less than 50%, for the other hand, a lot of valuable metal need to be processed, which increase the cost of retrieve."