Deformation Lines In Cold-Rolled Copper And Its Binary Alpha Solid Solution Alloys With Aluminum, Nickel And Zinc

DEFORMATION lines, also called etch markings or strain markings, are noneffaceable lines developed in individual grains by etching a metal specimen which has been cold worked sufficiently to cause atomic non-conformity or slight orientation differences within the grains. Etching occurs more rapidly at these lines of high chemical reactivity to produce a result similar to that revealing grain boundaries.1 Wider etching effects forming bands have been found. They are believed to be bands of deformation lines which form areas of measurably different orientation from the crystal matrix. The crystallite rotations causing these bands have been shown by Barrette to contribute to deformation textures. Although deformation lines have been observed in many metals, the amount of deformation required for their appearance has been established only in general terms. Mathewson and Phillips3 observed the first appearance of deformation lines in cold-rolled alpha brass at about 20 pct reduction in thickness using the standard ammonium hydroxide hydrogen peroxide etchant. Price and Davidson4 noted deformation lines in common high brass after 26.5 pct reduction by cold rolling using the same etchant. Johnson' observed dark thick forklike lines in 99.99 pct pure copper reduced 31.8 pct. Adcock6 observed deformation lines in 80-20 copper-nickel alloy rolled 50 pct. Samans7 found no deformation lines in alpha brass single crystals cold rolled 9.5 pct but they did appear after 25 pct reduction using ammonium hydroxide and hydrogen peroxide etchant. Barrett and Levenson8 observed deformation bands in drawn polycrystalline iron at very small reductions in area and noted that their initial appearance perhaps depends on grain size and other conditions. They reported deformation bands in a single crystal of iron reduced 6 pct by drawing. Brick9 noted that deformation lines in 70-30 brass apparently associated with {111} planes appeared after reductions of from 20-50 pct by cold rolling. Brick and Williamson10 noted that in single crystals of 70-30 alpha brass "as in polycrystalline brass, no deformation markings appeared until reductions exceeded 20 pct." Cook and Richards11 reported that in copper cold rolled less than about 50 pct few strain markings were apparent but for higher. reductions many strain markings appeared transverse to the rolled direction. In a review article Brick and Phillips12 noted that previous studies had not shown deformation lines in cold rolled alpha brass