Does Forging Increase Specific Density Of Steel?

THE writer has been unable to find much information relative to tests made to determine the effect of forging on the specific density of steel. The opinion, however, among men engaged in the business, seems to he that forging greatly compresses or consolidates the steel. While such is doubtless the case with spongy or porous steel, the following experiments indicate that there can be little or no change in the density with steel initially free from cavities: Ten ingots of basic open-hearth steel cast as shown in Fig. 1 were used in the experiments. All the specimens were 0.53 carbon with all other elements the same, the analysis being determined from drillings taken midway between the center and outside of the upper end, as shown in Fig. 2. The specimens were selected from over one thousand ingots so that the tests could be comparative for the work done in forging only, but no two of the ingots were cast in the same heat. Each ingot remained in the mold approximately 30 min., when it was removed and air-cooled. About 12 hr. later, when the temperature had been reduced to approximately that of the surrounding atmosphere, the head was discarded and the ingot heated in an oil furnace to approximately 2250° F. (1235° C). Approximately 1 min. was required to forge under the steam hammier to 1 ¼ in. (31.75 mm.), rough diameter, as shown by the dotted lines in Fig. 2. All ingots were allowed to air-cool after forging. Cylinders ½ in. (17.7 mm.) in diameter and ½ in. high were then turned from the forged and unforged parts of the ingots and numbered. The ten pairs of specimens were submitted to Louis E. Endsley, Professor of Railway Mechanical Engineering, University of Pittsburgh; A. N. Talbot, Professor of Applied Mechanics, University of Illinois; L. Z. Slater, chief chemist, Scullin Steel Co., St. Louis, Mo. No in-formation was furnished as to which specimens were forged or unforged and each laboratory used the same specimens, submitting the average of three independent determinations, a tabulation of which is shown in the accompanying table in which the laboratories are designated by