Effect of Different Refining Slag Systems on the Cleanliness of Molten Steel for Carbon Structural Steel

"The effect of two refining slags (A: 1.0–1.8 CaO/Al2O3 ratio, 11–20 wt% SiO2; and B: 1.0–1.2 CaO/SiO2 ratio, 25–35 wt% Al2O3) on the inclusion morphology of a carbon structural steel (Q235B) was studied by controlling the balance between the steel and the refining slag at 1600ºC in a Si–Mo resistance laboratory furnace. The results showed that most of the inclusions in the molten steel balanced with slag A were formed by a lowmelting CaO–MgO–Al2O3–SiO2 system with a total oxygen content (T[O]) being fixed at 6–13 ppm. The inclusions in liquid steel balanced with the slag B were mostly formed by the CaO–MnO–Al2O3–SiO2 system, with T[O] controlled to 19–26 ppm. The overall size of the inclusions under balance conditions was higher in the steel reacted with the slag B than that reacted with slag A, with the latter showing more inclusions smaller than 3 um. In order to generate a large number of spherical CaO–MgO–Al2O3–SiO2 inclusions smaller than 3 ??m while decreasing the T[O] in the resulting steel, the composition of slag A should be used. This composition allowed improving the cleanliness of the slab, and is also advantageous for the castability of the molten steel. IntroductionThe sample used in this study was a typical carbon steel manufactured by CQ Steel. The galvanized, tinned, and plastic composite steel plates made of the original plates are used extensively for decorative panels, general dust pipes, drums, instrument cases, switchboxes, and train cars, among other uses. The target control composition is shown in Table I. The S and P contents are usually fixed during production below 0.020 and 0.025 wt%, respectively, with the aim of reducing longitudinal cracks on the slab surface."