Effect of grain refinement on the tensile and fatigue crack growth properties of sand cast AM60 magnesium alloy

The effect of grain refinement on the tensile and fatigue crack propagation behavior of sand cast magnesium alloy AM60B has been investigated in the present study, C2Cl6 in the amount of 0,3% was used to grain refine the melt, The fracture toughness tests were conducted in laboratory air at room temperature (25°C) using a sine-wave cyclic frequency of 20Hz and a load ratio of R = 0,1, The response in the Paris's regime and the critical stress range were determined, Preliminary findings have shown that C2Cl6 has a significant effect on both the tensile properties and fatigue crack propagation of the alloy tested, Grain refinement increased both the yield and ultimate tensile strength by more than 46%, and decreased the crack growth rate from 2,7 to 1,4 MPa Vm , However, the grain size seems to have a smaller effect on threshold stress intensity factor range. The fracture surfaces of specimens were examined optically and under the scanning electron microscope (SEM) to determine the relationship between grain size and fatigue properties.