Electrochemical Behavior of an X-80 Pipeline Steel During Stress-Corrosion Cracking in Near-Neutral-pH Environment (PIPELINES FOR THE 21 ST CENTURY)

Electrochemical behavior of an X-80 pipeline steel, including frequency-sweep electrochemical-impedance spectroscopy (EIS), time-sweep EIS at a constant frequency and open-circuit potential (OCP) monitor, was investigated using four-point bending specimens subjected to a stress-corrosion cracking (SCC) test in a near-neutral pH environment. The capacitive loop became smaller with test duration, revealing an increase in the corrosion rate. The resistance obtained in the constant-frequency EIS test showed two regions, of which the region with a remarkable decrease in resistance transformed into a region of slow decrease, whereas the capacitance increased with test time indicating that iron dissolution was fast at first, and then a corrosion product or film formed and covered the surface, leading to the pitting formation.