Electrodeposition of Pb-Te-Tl Thermoelectric Materials

"By cyclic voltammetry and potentiostat electrodeposition using Potentiostat/Galvanstat, electrochemical behavior on Ag electrode in electrolyte 0.2M NaOH+0.01MPb(NO3)2-0.01M TeO2 -0.01M TlNO3 solution were also carried out at 298K. The processes of electrodeposition of Tl2Te3 and PbTl4Te3, a thermoelectric material, are reported along with analysis of the composition of the obtained deposits. The results showed that two different underlying processes are occurring depending on deposition potential. One process involves the reduction of TeO3 2- and Tl+ to Tl2Te3 in a potential interval of -0.70V < E < - 0.89V (vs. Hg/HgO). A second process at more negative reduction potentials involves reduction of TeO3 2-, Pb2+ and Tl+ to PbTl4Te3 in a potential interval of -1.02V < E < - 1.19V. The crystalline Tl2Te3 and PbTl2Te3 were deposited electrochemically on Ag substrates at -0.84V and -1.10V respectively. Thermoelectric (TE) material can form a temperature gradient across the material to make electric voltage, which is popular in waste heat utilization and recovery industry. Lead telluride, PbTe, is a small band gap semiconductor of 0.32eV at 300K. PbTe can change its n-type semiconductors with Pb-rich to p-type semiconductors with Te-rich[1]. And it is one of the best TE materials used in thermoelectric generators working between 500K and 600K, or even at a higher temperature of 800K.Three facto,rs play a role in the performance of a thermoelectric material: electrical conductivity (s), thermal conductivity(?), and the Seebeck coefficient (S). These can be combined with absolute temperature (T) to give a figure of merit (ZT) for the material, ZT = s2sT/?. By increasing the electrical conductivity and decreasing the thermal conductivity, which can enhance the ZT value, many efforts, such as alloying with other elements and making the materials nano-sized, have been done to improve its properties recently. Hsu et al. reported that the ZT value of Cubic AgPbmSbTe2+m is increased to 2.2 by doping Ag-Sb to PbTe.[2]."