Electron Microscopy Study of TiB Reinforced Nanocrystalline .Ti-MMC's Produced by Mechanical Alloying and Thermohydrogen Processing of TiH2-B Powder Mixtures

"Mechanical alloying (MA) synthesizing technology and thennohydrogen processing (THP) were utilized to produce nanocrystalline Ti-MMC's reinforced by TiB intermetallic compound by using TiH2-B powder mixtures. Powders MA'ed up to 8 hours were examined by X-ray diffraction and SEM study. All MA'ed powders afterwards were HIP'ed at 700, 800 and 950EC for 1 hour. Detailed XRD, SEM and TEM study of the samples were carried out to determine the structure and micrography of the Ti-TiB MMC material processed by MA+THP approach followed by HIP'ing at high temperatures.IntroductionThe fiber reinforced titanium base composites [1,2] which possess a great resistance to high temperature have been investigated. In these studies fibers of C and SiC were used as reinforcing materials. However, these fibers react with Ti-matrix at elevated temperature resulting in product formation at the interface between the matrix and the fiber. Because of the chemical reactions, strength of the product MMC material diminishes.In conventional techniques of whisker reinforced composite material production, the mixtures of matrix metal powders and dispersed fibers are consolidated by hot pressing, HIP and/or hot extrusion. These techniques, however, have some shortcomings. Hard and brittle fibers could be broken during mixing cycle of the processing. Consolidation techniques could also be the cause for fiber breakdown. Attaining of the uniform dispersion of fibers into the metal matrix is not an easy process. The chemical reactions at elevated temperature exposures in the interface between the matrix material and fiber reinforcement cause product formations leading to poor mechanical properties."