Equilibrium Between Free Cyanide And Gold Impregnated Activated Carbon (GIAC)

In parallel work, the cyanide/silver impregnated activated carbon system was studied for the purpose of developing an alternate cyanide removal system. It was found that free cyanide can be reduced from 20 ppm to below 10 ppb with a fixed bed of silver impregnated activated carbon, since such cyanide removal might be applicable to gold mill effluents, the investigation was extended to the cyanide/gold impregnated activated carbon (GIAC) system. Batch tests were conducted varying the gold content of activated carbon, carbon/CN ratio, stirring speed, pH of the initial solution, and the reaction temperature. The adsorption isotherm of cyanide/gold impregnated activated carbon system was also studied. The results of these batch tests show that the behaviour of the cyanide/GIAC system is very similar to the cyanide/silver impregnated activated carbon system variation of the gold content of the impregnated activated carbon has some influence on the cyanide adsorption rate. The latter is mainly increased, however, by increasing the GIAC/CN ratio. The activation energy was determined to be 3.12 kca1/mole (13.08 kj/mole) and the Au(CN)2 saturation at 194 µ M/g NORIT ROX O.B. The experimental results of reaction temperature and stirring speed show that the adsorption of free cyanide on such activated carbon is controlled by pore diffusion inside the activated carbon particle or by surface reaction. The adsorption isotherm follows the linear model and it is favourable for the cyanide/gold impregnated activated carbon system.