Extractive Metallurgy Division - A Study of the Sulfation of a Concentrate Containing Iron, Nickel, and Copper Sulfides

The effect of alkali sulfates in promoting the sul-fation of nickel and copper in a bulk sulfide flota -tion concentrate by fluidized bed roasting has been studied in the laboratory, and it was shown that the various alkali sulfates promote sulfation to approximately the same extent. The sulfation of a mixture of synthetically prepared iron and nickel oxide and of nickel ferrite has also been studied. Nickel sulfation was promoted by high ratios of Fe:Ni and by the presence of sodium sulfate. THE work described in this paper was a continuation of earlier studies into the role of alkali sulfates in promoting the sulfation roasting of nickel sulfides1,2 in an endeavor to determine how the system was affected by the presence of compounds of iron and copper. The earlier work1 showed that, in the sulfation of NiO at 680°C, the reaction was limited by the formation of an impermeable film of nickel sulfate on the oxide surface. The relative effect of the various alkali sulfates in promoting nickel sulfation varied in the order: Li > Na >Cs > Rb > K A study of alkali sulfate/ nickel sulfate interactions at high temperatures showed that the promoting action was due to the fact that the nickel sulfate product layer sintered and agglomerated only when the more active additives were present. This resulted in the formation of discontinuities in the nickel sulfate layer so that diffusion of the sulfating gases to the NiO surface was no longer impeded and the reaction could proceed to completion. A similar explanation was used for the observation that sodium and lithium sulfates promote the oxidation of NiS to NiO at temperatures below 750°C since small amounts of nickel sulfate were formed during oxidation.2 It was of interest to study the effect of alkali sulfates on the sulfate roasting of a sulfide flotation concentrate which is typical of material treated commercially. In order to control temperature it is essential to roast sulfides in a fluidized bed and this technique was therefore used, although the batchwise operation of a small-scale laboratory reactor does not reproduce all conditions which prevail in full-scale continuous plant. The results obtained are therefore only comparative, and cannot be used for predicting the optimum conditions for metal extraction. The sulfation of synthetically prepared mixed oxides of nickel + copper and nickel + iron and of nickel ferrite was also studied to evaluate the relative effects of alkali sulfates with more complex systems. SULFATION ROASTING OF A SULFIDE FLOTATION CONCENTRATE The bulk sulfide flotation concentrate used in this work contained 7.92 pct Ni, 1.74 pct Cu, 35.66 pct Fe, and 31.28 pct S. The sulfide minerals present in order of abundance were pyrrhotite FeS, pyrite FeS2, pentlandite (FeNi)S, and chalcopyrite CuFeS2. Two samples described as coarse and fine were used. The coarse sample, which was a flotation concentrate (58 pct plus 300 mesh), was ground to 100 pct minus 350 mesh to produce the fine sample. Before roasting, the sample of sulfide concentrate was agglomerated by wetting witli a solution of the alkali sulfate (or water), thoroughly mixing, and drying at 110°C. This gave a cake which was gently crushed and screened, the -18 +100 mesh fraction being used for fluidized bed roasting. A similar-size fraction had been used by the authors in pilot plant work with a 4-in.-diam fluidized bed reactor.' In this work it was found that the molar ratio of additive to the total iron + nickel + copper content of the sulfide sample should be adjusted to a value of approximately 0.06, as this was the optimum amount necessary for nickel sulfation. Experimental. The fluidized bed reactor consisted of a quartz tube approximately 60 cm long and 30 mm in diameter resting in a vertical tube furnace. The sulfide bed (30 g) was supported on a bed of -4 +12 mesh quartz particles 3 cm high, which rested on a sintered quartz disc welded to the tube. The temperature of the furnace was controlled with a variable transformer to give a final bed temperature of 680°C. The bed was fluidized with air or mixtures of air + 10 pct v/v SO2, at a total apparent gas velocity of 60 to 65 cm per sec at 680°C. The SO2 was introduced into the fluidizing air stream only when the oxidation of the sulfides was completed. At the end of the roasting period the calcine was leached with boiling water and the