Extractive Metallurgy Division - System Ag2O-B2O2; Its Thermodynamic Properties as a Slag Model

The oxygen pressure in equilibrium with silver and Ag2O-B2O3 melts has been measured between 800' and 900°C, to obtain the thermodynamic properties of the liquid. The compound Ag20. 4B20:1 appears to exist in the liquid, which shows marked heat content and entropy effects. A KNOWLEDGE of the thermodynamic properties of binary liquid silicates, borates, and phosphates would be of considerable assistance in the interpretation of the behavior of multi-component metallurgical slags. However, the literature contains comparatively few studies of the thermodynamics of binary slags. The system Ag20-B,O, attracted our attention as it was known to give a single liquid phase,',' in which high contents of silver could be obtained (up to 61 pct Ag according to Foex2). Further, it would be expected that the partial pressure of oxygen over melts in equilibrium with metallic silver could be used to determine the activity of Ag2O in the Ag,O-B,O, system. In many respects, it may be expected that the reaction of a basic oxide with boric oxide would be analogous to its reaction with silica. Liquid immiscibility frequently occurs in both borate and silicate systems. With B2O3 and SiO reaction with a basic oxide presumably involves a breakdown of the three-dimensional network of the acid oxide by reaction with oxygen atoms common to more than one silicon or boron atom. Ag2O-B2O3 was therefore investigated as a model of a slag system in the hope that its thermodynamic properties would assist in understanding those of other systems. Several methods for determining the activity of a component in a slag have been described in the literature. Chang and Derge" used high temperature electromotive force measurements to obtain the activity of SiO2 in CaO-SiO2 and Ca0-Al203-Si02 slags, but the cell reaction in their work is not clear. low has used rate of volatilization and vapor pressure measurements combined with phase diagrams to obtain activities in the systems KO-SiO,, Na,O-SiO, and Li,O-SiO," and PbO-SiO26 Taylor and Chipman7 extrapolated their results for the distribution of FeO between liquid iron and CaO (+Mg0)-FeO-SiOl slags to obtain the activity of FeO in the binary FeO-SiO2 system. In principle, one of the most direct methods for obtaining the activity of a metallic oxide in a phase is by comparison of the equilibrium oxygen pressure for the system metal-pure oxide with that of metal oxide-containing phase. Schenck and othersa have studied the stabilization of Ag2O on combination with other oxides (MO,) in the solid state by measurements of the oxygen pressure in systems of the type Ag-Ag,O-xM0,-MOy-0, (gas). Schuhmann and Ensio" have determined the activity of FeO in iron silicate slags in equilibrium with solid iron, using CO/CO2 mixtures to establish known partial pressure of oxygen. Although the method gives the activity of FeO without ambiguity, the slag is not a binary system, and interpretation of the results in terms of the hypothetical binary system FeO-SiO, is not possible. If a metal is solid at temperatures at which the properties of the slag containing its oxide are to be studied, this method has the considerable experimental advantage that the metal can be used as the container for the slag, and contamination by contact with refractories is avoided. In this work, crucibles for Ag2-B,O, melts were made from silver, and the liquid brought to equilibrium with definite pressures of oxygen gas. The oxygen pressure PO, thus fixes the activity of Ag20 in the liquid silver borate. For the reaction at a given temperature. is substantially constant, is directly proportional to the square root of the equilibrium oxygen pressure. Varying the oxygen pressure changed the silver oxide content of the liquid and it was possible to obtain the activity of Ag2O over a range of composition. Experimental Procedure In principle, the method consisted of bringing melts in silver crucibles or boats to equilibrium at a fixed temperature under a definite pressure of oxygen and analyzing the glass after solidification. Materials: B2O3 glass was prepared from A.R. quality boric acid by fusion in platinum. The silver