Formation of titanium aluminides and nickel aluminides intermetallic compound coatings on Inconel 738

Titanium aluminides and nickel aluminides offer the potentials, as coating materials, for high temperature and aerospace applications. In this research, attempt has been made to develop Al-Ti and Ni-Al intermetallic compound coatings on the surface of Inconel 738. The coatings applied through pack cementation and simultaneous diffusion annealing processes. Scanning-electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDAX) and grazing angle X-ray diffraction were used for evaluating of coating structure. It was demonstrated that the pack cementation technique could be used to develop TiAl3 and AlNi intermetallic compounds coating on Inconel 738 substrate. When pack cementation technique is based on a halide-activated pack with aluminum and titanium powders, the coating consists of TiAl3 intermetallic compound phase. Whereas, by pack aluminization of Inconel 738, the coating consists of AlNi intermetallic compound phase.