Fundamental Studies on Nickel Metallurgy in China

"The main processes for nickel metallurgy in China consist of electric arc furnace smelting to produce low grade nickel matte and converter to high grade nickel matte, grinding and flotation to separate nickel sulfide from copper sulfide and direct electrolysis of nickel matte. Systematic studies on the properties of electric furnace slag, smelting process for nickel matte, anodic process of nickel matte, cathodic process of nickel electrolysis have been done in our labs. In addition, an approach to a new hydrometallurgy process for nickel matte has been done. The feature of the new process is one stage acidic leaching of high grade nickel matte. The leaching solution could be purified by deposition way or by solvent extraction way. There are two leaching rate-determing steps, chemistry reaction-determing one at temperatures below 600C and diffusion-determing one at temperatures higher than 600 c. The acidic leaching fraction reacted dvaties with leaching time t according to the equation 1-(1- a ) 1/3=kt. The experimental data also show that the leaching reaction rate varies with concentrations of H+, Cl-, and it is also effected by copper sulfide and Cu++. The Cu++ ion can retard the leaching reaction due to forming a copper sulfide layer on the matte surface and the equation 1- 2/3 a. - (1- a: ) 2/3 akt can be used for the case. However the copper sulfide added into nickel matte can facilitate the leaching process. The research work for nickel metallurgy done by others in China has also been mentioned in this paper.Large scale production of nickel in China started in 1960s.The main processes consist of electric arc furnace smelting to produce low grade nickel matte and converter to high grade nickel matte grinding and floatation to separate copper sulfide from nickel sulfide and direct electrolysis of nickel matte.To reduce nickel loss in slag a reseaech group organized by Jinchuan Company and Central South Institute of Mining and Metallurgy (now the Central South University of Technology) measured the viscosity surface tention density conductance melting point and structure of the slag(I).lt has been found that the physico-chemical properties of the slag depend on the components SiO2 ,MgO and FeO but FeO in the slag is too high and the statistic analysis of data from industry gave an equation to correlate the content of Ni in slag with the content of Ni in matte and the composition of slag again it was pointed out that the content of FeO in slag effected the loss of Ni in slag very much (2). The ratio (FeO+MgO) to SiO2shouid be less than 1.13 and the content of Fe3O4should be as low as possible but the reaction"