Hot rolling process variable effect on the anisotropy of mechanical properties in Ti-6A1-4V alloy Hot rolling process variable effect on the anisotropy of mechanical properties in Ti-6A1-4V alloy

Rolling temperatures and cross rolling ratios were varied to investigate the effect of crystallographic texture of alpha-phase on the anisotropy of mechanical properties in modified Ti-6A1-4V alloy. Hot rolling method was unidirectional and cross rolling, during which the rolling temperature was in the range of 830°C and 920°C. Cross rolling ratios were varied from 0.3 to 1.0 at 875°C. For unidirectional rolling, as the rolling temperature increased texture changed from the mixed basal and transverse texture to the simple transverse texture. Contrary to other work, it was observed that the maximum intensity of transverse components increased with the increase in rolling temperature. For cross rolling, on the other hand, the transverse texture component was almost suppressed at 830°C, giving rise to a symmetrical basal texture. With increasing cross rolling temperature, the transverse texture components developed again. A simple transverse texture, which showed two maxima appearing circularly 90° apart, was observed at 920°C. It was found that unidirectional rolling could not eliminate the transverse texture, which resulted in the anisotropy of mechanical properties. The anisotropy of mechanical properties obtained from tensile and V-notch Charpy test was closely related to the crystallographic texture and its intensity at each rolling condition. To obtain the isotropy of mechanical properties by cross rolling, it is suggested that cross-rolling ratios should be controlled above 0.5. The variation of rolling temperatures and directions has great influence on the anisotropy of impact value rather than tensile strength.