Industrial Minerals - Measurement of Cement Kiln Shell Temperatures (Mining Engineering, Feb 1960, pg 164)

At Buffington Station, Gary, Ind., Universal Atlas Cement operates fourteen 8 x 101/2 x 155-ft cement kilns in mill 6 and two 11 x 360-ft kilns in the Harbor plant. The No. 11 and 12 kilns in mill 6 are equipped with Manitowac recuperator sections. This report describes studies in measuring exterior shell temperatures on several of these kilns and the development of a traveling radiation pyrometer with certain novel features. Preliminary Work: At first various temperature-sensing devices were placed on the steel shell: 1) crayons with calibrated melting points, 2) colored paints with temperature-calibrated pigments, 3) aluminum paints with temperature-calibrated binders, and 4) metal-stem dial thermometers. The colored paints and aluminum paints failed to indicate the temperatures correctly. The crayons and thermometers did indicate fairly correct temperatures, but it proved impossible to apply enough of these on the shell to detect all the potential areas where hot spots might develop. Furthermore, considerable labor was required to apply these sensors and read the temperatures. Consequently no further work was done with these devices. Formation of Hot Spots: In the burning or clinker-ing zone of a cement kiln, the thickness of the protective coating and thickness of the brick govern the amount of heat transmitted to the steel kiln shell. Usually the protective coating consists of 4 to 8 in. of fused cement clinker. The formation of a hot spot is usually caused by loss of coating? that is, localized areas of the coating become thin or fall away from the refractory. This is generally caused by excessive temperature in the burning zone over a fairly long period of time. It may also be caused by a sudden thermal change in the burning zone. Variations in raw feed composition and in feed rate require changes in the fuel and air rates, and when these are not appropriately altered, conditions may develop in the kiln that will result in loss of coating. Luminescence on the kiln shell indicates that a hot spot has developed to a point that usually alters the refractory's thermal conductivity properties. When this thermal weakness zone occurs in the burning zone of the kiln, constant vigilance is required to protect it by maintaining proper coating. Even so, it has been the writers' experience that within a period of several days to about four weeks the hot spot usually recurs with greater severity. This necessitates shutting down the kiln and re-bricking the affected area. One of the prerequisites of a good burnerman is the ability to maintain a protective coating despite the many variables in operation. When he knows that it is getting thin or that an area has dropped off, he reduces the firing rate and kiln speed and brings feed into the affected area in an effort to rebuild the coating. But when powdered fuel is burned, the atmosphere of the kiln may prevent the burnerman's observing the condition of the coating closely at all times without taking off the fire. It is not considered good practice to do this frequently, as it imposes a thermal shock on the coating and upsets operation of the kiln. To help the burnerman scan the shell of the kiln along the burning zone, therefore, a radiation pyrometer, connected to a potentiometric recorder, was mounted on a slowly moving steel cable. The theory of operation, construction details, and adaptability of the radiation pyrometer are included in an excellent monograph' and also in a textbook.' Shell temperatures of the Atlas Cement kilns were measured with a Brown Instruments Div. low intermediate range Radiamatic unit, of range 200" to 1200°F, and a circular chart Electronik potentio-metric recorder, of range 500" to 1000°F. In Bulletin 59095M the supplier publishes standard calibration data (millivolts vs degrees Fahrenheit) for this radiation pyrometer, These data, however, apply only to flat surfaces having emissivities of unity. Calibration of Radiation Pyrometer for Use on Curved Surfaces: When applied to surface temperature measurements, the radiation pyrometer reading depends on the nature of the surface, the material of which it is composed, and also to some extent on the temperature of the surroundings. Although the present radiation pyrometer is designed to give a calibrated response under ideal (black body) conditions when used commercially, it must be calibrated empirically. The calibration procedure, given below, follows that described by Dike (Ref. 1, pp. 38-39). Calibration tests on plane and curved surfaces showed that the response of the radiation pyrometer was very