Institute of Metals Division - A Reinvestigation of the Systems Ti-Cr and Ti-V, Felix Ermanix

The systems Ti-Crand Ti-Vhave been reinvesti-gated in the region up to 40 wt pct alloying addition using both conventional and rapid quenching techniques. The Ti-Cr eutectoid temperature was determined to be at 667° & 10° C and 14.5 wt pct Cr. The solubility of the Cr in a Ti was found to be less than 1 pctat 700"C. The P transus of the Ti-V system was found to be depressed to 510°C at 40 wt pct V and the solubility of V in a Ti was found to be less than 2 wt pct at 700°C. Investigation by a. d. McQuillan1-3and m. k. McQuillan4 on the systems Ti-Co, Ti-Cr, Ti-Cu, Ti-Fe, Ti-Mn, Ti-Ni, and Ti-V has cast doubt as to the position of the ß/a + ß boundaries in many of these systems. Their investigations were carried out using hydrogen pressure and/or rapid quenching experiments, as opposed to the conventional quartz capsule techniques employed by most other investigator.'" By these methods, the ß/a + ß boundary was found to be lower than that obtained by conventional techniques in all except the Ti-Fe system. In the latter, the ß/a + ß boundary was essentially the same as the boundary obtained by conventional technique.7' On the basis of rapid quenching results in the Ti-Cr system, M. K. McQuillan4 placed the eutectoid temperature below 550°C whereas other investigations using conventional techniques had placed the eutectoid variously as between 650' and 700°C,5 between 675' and 700°C,6 between 650" and 675°C,7 at 670°C,8 and above 625"C.la9l3 In order to check these results, a reinvestigation of four of the systems was undertaken using both conventional and rapid-quenching techniques. The Ti-Fe and Ti-Mn systems will be dealt with in anoth er paper, with only the Ti-Cr and Ti-V systems being discussed here. EXPERIMENTAL TECHNIQUES Alloys employed for the delineation of the systems under investigation were prepared from iodide titanium sheet capsules containing the alloying materials,