Institute of Metals Division - Blended Aluminum- Powder Products ( TN)

Dispersion-strengthened sintered aluminum products are normally manufactured from surface-oxidized aluminum powder, SAP,' or from atomized aluminum powder.' The powder-blending technique consisting in mechanical mixing of the constituents has been used in the manufacture of numerous dispersion-strengthening alloys, but has never been successfully applied to aluminum alloys. This technique may, however, be applicable if it is possible to produce an unagglomerated mixture of the constituents in the form of fine powders, and the present study was initiated to test this assumption in the aluminum/aluminum oxide system.3 Table I lists the two grades of aluminum powder and the aluminum oxide powder used in the manufacture of the alloys. MD 105 A is an aluminum powder with an average grain size less than 5 IJ., which is isolated from the MD 105 powder by centrifugal separation in cyclohexanol. The aluminum powders and the aluminum oxide were blended in a high-speed blender and then subjected to cold compaction and hot compaction at 550" to 600°C. Subsequently the compacts were hot-extruded with an extrusion ratio of 15 to 1. The alloys were evaluated by tensile testing at room temperature and at 400°C, microscopic examination, and heat treatment at 500°C followed by tensile testing at room temperature. For the purpose of comparison, a commercial SAP quality supplied by Swiss Aluminium Ltd. was tested in the same manner. The tensile data at room temperature and at 400°C are plotted in Figs. 1, 2, and 3 as a function of the weight percent of oxide. The oxide content