Institute of Metals Division - Creep Behavior of Zinc Modified by Copper in the Surface Layer

THE modern theories of creep¹-4 in general have been based upon the concept of generation and migration of dislocations, with the generation process normally assumed to be rate controlling. The theories are generally deficient in that they fail to take into account many factors that are known to influence creep. The influence of the state of the surface of the test specimen has been almost completely overlooked; yet the present report shows that the nature of the surface may, in certain cases, govern the creep characteristics of a specimen. In the period since Taylor" applied the concept of dislocations to a study of metals, a school of thought has developed that closely relates the plastic deformation of metals to the generation and migration of dislocations through the crystal lattice. It might be expected that the thermal energy required for the generation of a dislocation would be different from that for migration of the dislocation through the lattice. Furthermore, the activation energy for generation would be expected to vary for different parts of the solid metal. It has been predicted that dislocations would be generated most easily at external surfaces, but could also be activated at certain internal surfaces such as grain or phase boundaries. Within the body of the metal a range of values for the activation energy might be expected because of different degrees of disorder at such regions as grain boundaries, impurities, and second-phase particles. The particular value of the activation energy that was rate determining could then depend on the specific conditions of a test. If, for example, the surface atoms were by some means constrained, the generation of dislocations in the body of the metal might become the important factor. On the other hand, other conditions may favor generation at the surface. It is possible then that the creep behavior may not be completely determined by the inherent properties of the metal. Even the environment in which a test is carried out could have a significant effect. In fact it is conceivable that in order to obtain the maximum creep resistance from a given alloy, the surface atoms must be so constrained that the activation energy for generating dislocations on the surface is at least equal to that required for generation in the body of the metal. On the basis of such considerations, and in view of the limited number of publications discussing this subject, it seemed that an investigation of the influence of the state of the surface on creep might yield information of both theoretical and engineering interest. Experiments on single crystals, demonstrating a variation in the mechanical properties due to alterations in the surface layer, have been reported by several investigators.6-13 he results of these experiments have been briefly summarized;14 consequently, the earlier work will not be reviewed here. As an example of these findings the observations of Cottrell and Gibbons may be cited. They reported the critical shear stress of a lightly oxidized cadmium single crystal is greater by a factor of 2½ than a specimen with a clean surface. Materials and Methods Single crystals M in. in diam and 8 in. long were prepared from Horse Head Special zinc, melted under an atmosphere of helium in a large pyrex test tube, and drawn up into a long ½ in. diam pyrex tube by means of a vacuum pump. The cast zinc rods thus produced were cut into convenient lengths and sealed in evacuated pyrex tubes. Single crystals were grown by gradual solidification of the remelted rods. Cleaving the ends of the single crystal specimens chilled by liquid nitrogen proved a simple method for determining orientations from the exposed basal plane from the markings left on the cleaved surface that gave the slip directions with sufficient accuracy for the experimental work. The specimens chosen for the experiments were those having the angle between the basal plane and the specimen axis within the range of 15" to 65". Since zinc single crystals are quite delicate, it was necessary to devise an appropriate method of gripping the specimens in order to suspend them in the furnace and apply the load. Stainless steel collars were prepared having an inside taper, the smaller end of the taper being of such a size that the specimen could just pass through freely. The tapered hole did not extend the full length of the collar; a sufficient thickness of metal remained so that a hook could be attached to provide a means of applying the load and suspending the specimen. One of the collars was slipped over the upper end of a specimen which was supported vertically in a steel jig. The collar was then heated electrically until the end of the crystal melted and filled the collar with molten zinc. At this point the application of heat was discontinued, whereupon the molten zinc quickly solidified, due to the chilling effect of the jig. The specimen was then inverted and the second collar applied in a similar manner. The jig served several purposes: limiting the length of specimen that was melted, providing excellent alignment of the collars with respect to the specimen axis, and protecting the specimen from mechanical damage. Once the specimen was suspended in the furnace and loaded, it was desired to accomplish the surface treatment with a minimum of disturbance of the specimen. Around the specimen was a long pyrex tube, the upper portion of which was approximately 1 in. in diam, and in it was a copper coil of such a diameter to fit snugly against the tube. A specimen, approximately ½ in. in diam and 4 in. long, was suspended by means of a stainless steel rod so that it hung within the copper coil. The lower portion of the glass tube was approximately ¼ in. in diarn, and passing through it was a 5/32 in. diam stainless steel rod which hung from the lower specimen collar. This portion of the glass tube and the stainless steel rod extended through the bottom of the furnace. A T-connector, with suitable packing, was attached to the lower end of the stainless rod to provide a water-