Institute of Metals Division - Deformation Mechanisms of Alpha-Uranium Single Crystals

The operative deformation elements in a-uranium single crystals under compression at room temperature have been determined as a function of the compression directions. The deformation mechanisms noted may be arranged with respect to their frequency of occurrence and ease of operation in the following order: 1 — (010)-[I001 slip, 2—{130} twinning, 3—{~172} twinning, and 4bunder special conditions of stress application, kinking, cross-slip, {.-176) twinning, and (011) slip. The composition planes of the (172) and (176) systems were found to be irrational. Cross-slip was shown to be associated with the major (010) slip system, coupled with localized interaction of slip on the (001) planes. The mechanism of kinking was found to be similar to that observed in other metals in that it occurred chiefly when the compression direction was, nearly parallel to the principal slip direction [loo] and was associated with a lattice rotation about an axis contained in the slip plane and normal to the slip direction: the [001] in the uranium lattice. The resolved critical shear stress for slip on the (010)-[100] system was found to be 0.34 kg per mm2 In a single test it was shown that under compression in suitable directions twinning on the (130) also occurs at 600°C. DEFORMATION mechanisms of large grained polycrystalline orthorhombic a-uranium have been studied by Cahn.1 A major slip system identified as the (010) with a probable [loo] slip direction and a minor slip system on the (110) planes were reported; the slip direction of the minor system was not determined. The twinning systems that were identified experimentally included the (130) and the irrational (172) composition planes; observations of other traces which were not as frequent and which did not lend themselves to positive experimental identification led Cahn to postulate on the basis of indirect evidence that twinning also occurred on (112) and (121) planes. In addition to the foregoing slip and twinning mechanisms, Cahn also observed kinking and cross-slip in conjunction with the major (010) system; the cooperative cross-slip plane was not identified. The availability of single crystals to the present authors has enabled them to check these results, particularly with reference to the doubtful mechanisms and the preference of operation of any one mechanism in relation to the direction of stress application. The tests were confined to compression only, primarily because of experimental limitations imposed by the size and shape of the available crystals. The tests were performed at room temperature except for one crystal compressed at 600°C. The compression directions were chosen to obtain a representative coverage of one quadrant of the stereo-graphic projection. To test the existence of some of the deformation elements that were reported by Cahn, but were not found in the present study, several additional crystals were compressed in specifically chosen directions considered most ideal for their operation. Experimental Techniques The single crystals were obtained by the grain coarsening technique described by Fisher? They grinding and polishing on rotating laps, with final surface preparation performed in a H3PO4-HNO3 electropolishing bath. A typical crystal readied for compression is shown in Fig. 1; their dimensions were rather small and depended upon the testing direction. Crystals isolated for compression in a direction close to the [010] axis, which lay roughly parallel to the longitudinal axis of the polycrystalline rod, were about 3 to 4 mm long and 5 mm2 in cross-section, while those prepared for compression in other directions were smaller. Most of the crystals were free from twin markings and showed no evidence of Laue asterism. Several crystals, however, contained twin traces prior to compression; these were identified prior to compression so as to clearly distinguish them from those initiated during deformation. The origin of the twin markings prior to deformation may be ascribed to two sources: thermal stresses and specimen handling during isolation and preparation. Two other types of imperfections in the crystals should be mentioned: inclusions, which were probably oxides or carbides. and three of the crystals contained a small number of spherical included grains (<0.01 mm diam), which were remnants of unabsorbed grains from the coarsening treatment. The volume represented by these imperfections was small, and their presence presented no difficulties in the interpretation of the macrodeformation processes during subsequent compression. Two compression fixtures were employed: crystals A, B, C, E, and G were compressed in a hand-operated screw-driven jig whose compression platens were designed to minimize axial rotation;