Institute of Metals Division - Effects of Metallurgical Variables on Charpy and Drop-Weight Tests

Twenty-nine laboratory steels were studied to determine the effects of composition and ferrite grain size on drop-weight and Charpy V-notch transition temperatures. The experimental steels covered the following ranges in composition.. 0.10 to 0.32 pct C, 0.30 to 1.31 pct Mn, 0.02 to 0.43 pct Si, md nil to 0.136 pct acid-soluble Al. Although most of the data were obtained on hot-rolled samples, some plates were heat-treated in order to cover a wider range in ferrite grain size. The experimental data were used for a multiple-correlation analysis conducted with the aid of an electronic computer. The study showed that carbon raises and that manganese, silicon, aluminum, and finer ferrite grains lower both drop-weight and Charpy transition temperatures. Quantitatively, variations in composition and grain size have a more marked effect on V15 Charpy transition temperatures than on the drop-weight transition temperature. Useful correlations were found between transition temperatures in drop-weight tests and those defined by seven different criteria for Charpy tests. Evidence was accumulated that the conditions ordinarily used for drop-weight tests are more severe for 1-1/4-in. -thick plate than for 5/8- to 1-in. -thickplate. PROJECT SR-151, to study quantitatively the effects of metallurgical variables on performance in the drop-weight test, was established by the Ship Structure Committee late in 1958 on recommendation of the National Academy of Sciences, National Research Council. This project was initiated as a result of the increasing use of the drop-weight (nil-ductility) test in predicting the ductile-to-brittle behavior of steel. Qualitative data indicated the drop-weight was not as sensitive to metallurgical variables as the Charpy V-notch test. Furthermore, the available information indicated that the drop-weight test did not show the superiority of killed steels over semikilled steels reflected by Charpy tests. This difference in sensitivity to brittle fracture is considered important because the drop-weight transition temperature has been reported1 to correlate better with service-temperature failures than the V-notch test does at a constant energy level. Therefore, this project was concerned with establishing quantitatively the effects of metallurgical variables in the drop-weight test. For comparison, Charpy V-notch data were obtained for the steels investigated. This paper summarizes the results of the investigation. Most of the steels used for the study were made and processed in the laboratory. However, some tests were also made on commercial killed steels available from Project SR-139 (SSC-141). During the course of the investigation, data were obtained on the effects of carbon, silicon, manganese, and aluminum on transition temperatures of drop-weight and Charpy specimens. In addition, the effects of heat treatment which changed the ferrite grain size and the transition temperatures were also investigated. Finally a few exploratory studies were made on commercial killed steels to evaluate the effects of plate thickness, grain size, and heat treatment on the performance of drop-weight specimens. EXPERIMENTAL PROCEDURES Preparation of Materials. A total of twenty-nine 500-lb induction-furnace heats were made and processed in the laboratory for the investigation. Carbon, manganese, silicon, and aluminum contents were systematically varied. Melting and rolling techniques proven satisfactory in a previous project2 were used as a guide for the current investigation. Composition. The composition of the twenty-nine laboratory heats made for this project are given in Table I. The steels are divided into three groups. The first group consists of ten aluminum-killed steels similar in composition to Class C ship-plate steel. The second group consists of ten semikilled or Class B type steels. In both of these groups the carbon and manganese contents were intentionally varied over a wide range. This wide range in composition was helpful in obtaining quantitative data from a limited number of steels. The primary purposes of these two groups of steels was to determine the effects of carbon, manganese, and deoxidation practice. In addition, one steel in each group (Steels 2-2 and 9-2) were made about 1 year after the start of the program in order to check consistency of melting practice. The third group of nine steels listed in Table I was intended for studies on the effects of silicon and aluminum. In eight of these steels carbon and manganese were held relatively constant at levels of about 0.2 and 0.8 pct, respectively, while silicon and