Institute of Metals Division - Investigation of the Vanadium-Manganese Alloy System

The phases occurring in the V-Mn system were studied by means of X-yay diffraction and metallo-paphic techniques, using are-melted alloy specimens annealed in the temperature range 800° to 1150°C and quenched. The bcc solid solution extends at 1250°C all the way from vanadium to 6-manganese. Below 1050°C the a-phase is formed, and the terminal a-manganese phase is stabilized up to about 900°C by vanadium in solid solution. IN the only previous general survey of the V-Mn system Cornelius, Bungardt and Schiedtl reported the existence of three intermediate phases corresponding to the approximate compositions VMn,, VMn, and V5Mn. The phase VMn8 has recently been identified as a o phase2 but the alloy VMn was found to have a bcc structure2 corresponding apparently to the vanadium solid solution rather than to the large cubic unit cell reported by Cornelius et al. 1 Subsequent work by Rostoker and Yamamoto3 has shown that the vanadium-base bcc solid solution extends to at least 15 pct Mn at 900°C. An alloy corresponding to the composition VMn, was examined by Elliott,4 who reported that the as-cast sample as well as samples annealed at 1200o and 1300°C had bcc structures, but that annealing at 1000°, 800") and 600°C produced two phases. One of these phases was apparently the bcc solid solution and the other resembled the o phase structure. Hellawell and Hume-Rothery5 established the phase relationships in manganese-rich alloys above 1000°C, and showed that the o phase in this system is replaced by the 6 Mn (bcc) solid solution at temperatures above 1050°C. These results suggest that a continuous bcc solid solution may exist above 1050°C between vanadium and 6 Mn. The present investigation was undertaken in order to develop more complete information in regard to this system. EXPERIMENTAL METHODS The alloys used in the present work were prepared by arc-melting electrolytic manganese having a minimum purity of 99.9 pct and vanadium lumps with a purity of 99.7 pct. The major impurities present in these metals were carbon, nitrogen, and oxygen and this would account for the small percentage of nonmetallic inclusions observed metal-lographically. The arc-melting was at first performed under a helium atmosphere and it was necessary to keep the melting times as short as possible in order to minimize the loss of manganese by vaporization. It was later found that the evaporation of manganese was considerably reduced when the melting was done under argon atmosphere. The final composition of each alloy was calculated by assuming that the total weight loss during melting was due to evaporation of manganese. Compositions which were calculated in this manner agreed reasonably well with the results of chemical analysis, as shown in Table I. Spectrographic analysis revealed the presence of contamination by tungsten, but in no case was the percentage of tungsten greater then 0.4 at. pct. The specimens were in each case broken in half and the fractured section was examined visually and microscopically for evidence of inhomogeneity. Each specimen was homogenized at temperatures near l100°C, as shown in Table I. After this treatment most specimens consisted of large columnar grains of the bcc vanadium solid solution. The etchant used in most of the metallographic work consisted of 20 pct nitric acid, 20 pct hydro-flouric acid, and 60 pct glycerine. It was found that this etchant would clearly delineate the phases present in these alloys although it does not produce any striking contrast between the phases. For certain manganese-rich alloys, a 1 pct aqueous solution of nitric acid was used. This etchant gave a brown color to the a-manganese phase, whereas the o phase was virtually unattacked and appeared very light as shown in Fig. 1. The etchants used by Cornelius et a1.l were found to produce spurious effects in some of these alloys. In particular, the vanadium-rich alloys etched in hot sulfuric acid often appeared to consist of two phases when both X-ray diffraction and etching with the glycerine-acid mixture indicated the presence of single phase bcc solid solution. A few percent of what appears to be an oxide or nitride phase was found at the grain boundaries and in the interior of the grains, especially in the vanadium-rich alloys. All alloys were annealed in sealed silica tubes containing 1 atm of pure argon and these tubes were then quenched in cold water. Although some manganese loss occurred during annealing, the loss seemed to be confined to the surface of the speci-