Institute of Metals Division - Observations on the Recrystallization of a Silicon-Iron Crystal in a Polygonized Matrix

Observations were made on the recrystallization of a 70 pct cdd-rolled silicon-iron crystal with an initial orientation of (113) [332]. Its polygonization and recrystallization characteristics were studied. Results indicated that re crystallization tendency of the deformed crystal is much weakened by the polygonization of the matrix. Complete recrystallization in such specimens is achieved by the growth of recrystallized grains of sufficient size and of the right orientations in relation to the matrix. Evidence was also furnished which suggests that the difference in the re-crystallization tendency is a result of the difference in the severity of lattice bending rather than the difference in orientation of the deformation texture. DUNN and Koh1,2 have made an extensive study on the rolling and annealing textures in silicon-iron crystals. Their results indicated that the recrystallization tendency can be widely different in crystals with different orientations. A particularly interesting example of their results was a crystal with an initial orientation of (113) [332], which developed a deformation texture of (001) [110] after 70 pct cold-rolling. Recrystallization in this crystal took long time anneals at high temperatures. Other crystals having different orientations recrystallized very rapidly. Wiener and corcoran3 have observed the retention of the (100) [011] deformation texture in a low-temperature annealed specimen of a commercial silicon-iron alloy, corresponding to areas of light-etching low-angle boundaries in the annealed struc-