Institute of Metals Division - Preferred Orientations in Iodide Titanium (Discussion page 1563)

The wire textures for cold rolled and recrystallized iodide titanium and the sheet textures for this material produced by cold and hot rolling, and recrystallization at a series of temperatures were determined. &apos;The effect of the a + ß transformation on the sheet texture was noted. UNTIL recently it was believed that all hexagonal close-packed metals deformed by slip on the basal plane, (0001), and that rolling should tend to rotate this slip plane into the plane of the rolled sheet. The pole figures of cold rolled magnesium&apos; are satisfactorily explained on this basis. There is a tendency for the <1120> directions to align parallel to the rolling direction, and the principal scatter is in the rolling direction. Zinc% as a rolling texture in which the hexagonal axis is inclined 20" to 25" toward the rolling direction. Twinning is believed to account for the moving of the basal plane away from parallelism with the rolling plane. The texture of beryllium3 places the basal plane parallel to the rolling plane with the [1010] direction parallel to the rolling direction, and the scatter from this orientation is primarily in the transverse direction. Cold rolled textures reported for zirconium&apos; and titanium5 how the [1010] directions to lie parallel to the rolling direction and the (0001) plane tilted by approximately 25" to 30" to the rolling plane in the transverse direction. Rosi has recently reported that the mechanisms for deformation in titanium are distinctly different from those commonly reported for hexagonal close-packed metals. The principal slip plane is the prismatic plane, {1010), with some slip also occurring on the pyramidal planes, (1011). However, there is no evidence for basal slip. The slip direction is reported to be the close-packed digonal axis, [1120]. In addition to the twin plane commonly reported for metals of this class, {1012), Rosi found the twin planes (1122) and {1121), with the dominant twin plane being (1121). Information regarding the recrystallization and hot rolling textures of hexagonal close-packed metals is limited. Barrett and Smigelskas report that rolling beryllium at temperatures up to 800°C and recrystallization at 700°C produce textures not differing from the cold rolled sheet texture.3 McGeary and Lustman find that hot rolling at 850°C produces the same basic texture in zirconium as rolling at room temperature.&apos; These investigators also report that the texture for sheet zirconium recrystallized at 650 °C differs from the cold rolled orientation inasmuch as the [1120] direction, instead of the [1010] direction, is parallel to the rolling direction. In the case of titanium, it is not possible to deduce which direction is preferred in the recrystallized state from the pole figures presented by Clark." The purpose of this paper is to report an extensive investigation of the preferred orientations in iodide titanium. Since the deformation mechanisms for titanium are different from those commonly given for hexagonal close-packed metals, it is not surprising to find distinct differences between the textures of titanium and other metals of this class. Materials and Methods This investigation was carried out on iodide titanium obtained from the New Jersey Zinc Co. with an analysis as follows: N2, 0.002 pct; Mn, 0.004; Fe, 0.0065; A1, 0.0065; Pb, 0.0025; Cu, 0.01; Sn, 0.002; and Ti, remainder. The crystallities of titanium were broken from the as-deposited bar and melted to form 20 g buttons on a water-cooled copper block in a vacuum arc-furnace. Hardness tests conducted on the material before and after melting differed by only two or three Vickers Pyramid Numbers, indicating no or insignificant contamination. The buttons were hot forged, ground, and etched to sizes and shapes suitable for the rolling schedule, and vacuum annealed at 1300°F. Specimens for determination of the wire textures were reduced 91 pct in diameter to 0.027 in. in 24 steps using grooved rolls. In order for the orientation of the central region to be studied, portions of these wires were electrolytically reduced to a diameter of 0.005 in. using the procedure described by Sutcliffe and Reynolds.&apos; The sheet textures were determined on titanium cold rolled 97 pct to a thickness of 0.005 in. A reduction of approximately 10 pct per pass was used, and the rolling direction was changed 180" after each pass. Specimens used for determination of the recrystallized textures were annealed in evacuated quartz tubes at 1000°, 1300°, and 1500°F. The grain size of the 1000°F specimen was sufficiently small to give satisfactory X-ray patterns with the specimen stationary. However, it was necessary to scan the surface of the other recrystallized specimens. The microstructure of each annealed specimen was that of a recrystallized material. The diffraction rings all showed the break-up into spots typical of recrystallized structures.