Institute of Metals Division - Recrystallization of Iron and Iron-Manganese Alloys (Discussion)

W. M. Williams (McGill University)-The authors are to be congratulated on completing this detailed investigation of recrystallization behavior. The present writer has recently completed some research at the University of Toronto on the recrystallization and grain growth behavior of a number of "pure" irons, and he would like to take issue with the authors' contention that recrystallization cannot be followed by means of hardness measurements. Two series of specimens of Ferrovac E, a com- mercially available iron, were annealed to complete recrystallization at 525" and 620" C, measurements being made both of Rockwell hardness and of volume percent recrystallized as a function of annealing time. Good correlation was found between these two quantities and, following the earlier practice of Cook and Richards for copper, hardness measurements were used in an extensive investigation of recrystallization. No anomalous behavior was observed as a result of this practice. Specimens which showed complete softening always showed, (metallographically and by X-rays), completely re-crystallized structures. These observations do not, of course, detract in the least from the results of the work under discus-