Institute of Metals Division - Role of Dilute Binary Transition Element Additions on the Recrystallization of Vanadium

The effect of transition element binary solid-solution additions upon the recrystallization temperature of vanadium has been investigated. Cr, Fe, Co, Ni, Mo, Ru, Rh, Os, and IY lower the recrystallization temperature, while Ti, Mn, Zr, Cb, Pd, Hf, Ta, W, Re, and Pt raise it. The majority of elements have their greatest effect in less than 0.15 at. pet. Both the rate of change of recrystallization temperature with atomic percent solute and the limit of initial linearity are found to Correlate with the free atom grozdnd state outer electron configuration of the sollte element. THE work of Abrahamson and Grant1 and Abraham-son and Blakeney2 has shown that the solute's elec- tron configuration appears to be a prime determinant of both brittle-to-ductile transition and recrystallization temperature in dilute binary alloys. It has also been shown by Abrahamson3 that the limit of linearity, i.e., the limit of initial linear change of recrystallization temperature with atomic percent solute, is also a function of the electron configuration of the solute in iron base alloys. Because of the systematic nature of the solute electron configuration correlation, it is to be expected that some systematic variation might be observed upon changing the solvent. Thus, this study of recrystallization in vanadium base alloys is the first of a series aimed at defining the role played by the electron configuration of solute in determining the recrystallization characteristics of dilute transitional alloys. PROCEDURE All alloys were made using 99.8 pct V containing 0.011 C, 0.024 N, 0.08 0, 0.006 H, 0.035 Ta, and