Institute of Metals Division - Solid Solubility of Cementite in Alpha Iron

THE solid solubility of cementite in a-iron has been investigated a number of times and there is now general agreement on the solubility of about 0.018 wt pct at the eutectoid temperature, 720°C. With decreasing temperature, the solubility falls off so rapidly and to such a low value that no data obtained by standard metallurgical methods are available below 500°C. Using a new technique, however, Dijkstral has obtained apparently accurate solubilities down to 400°C; which data agree well with previously measured solubilities in the 600" to 700°C temperature range.' The present paper has in part the purpose of extending his work to still lower temperatures. Earlier work of Low and Gensamer3 on iron has established that the presence of a relatively small amount of carbon can play a tremendous role in affecting the mechanical properties. In particular they found that the yield point remained high as they reduced the amount of carbon in the iron; the yield point dropped only after the carbon content had fallen to something less than 0.003 wt pct, the point where their carbon analysis failed. It seemed desirable to the present author to see if some means could not be found to extend this part of their work. This investigation has then the additional purpose to determine the range of carbon concentration in which the major change occurs. Solubility The method used in the present work to measure small percentages of carbon in a-iron utilizes internal friction. Since this method may not be fa-miliar to the reader, the following explanation will be given (a part of this procedure is from unpublished results of Dijkstra): It is known that the internal friction associated with the diffusion of