Institute of Metals Division - Surface Orientation and Rolling of Magnesium Sheet

Magnesium alloy sheet has less ability to accept bending at room temperature than most of the heavier metals. In work designed to improve the bend properties, the preferred orientation of the sheet is of major importance as it is in all studies of the properties of wrought magnesium products. When rolled into sheet, all of the common magnesium alloys form an orientation texture having the basal (002) planes approaching parallel to the surface of the sheet. This texture is only slightly affected by annealing. Magnesium single crystals are highly anisotropic, and, as might be expected, so are magnesium alloy wrought products in which a strong preferred orientation is developed. It is therefore not surprising that bend properties are affected by orientation. Ansel and Betterton1 reported that the orientation of AZ3lXt sheet varies from surface to center and that bend properties are improved by etching away the sharply oriented material at the surface of the sheet to reach the more broadly oriented structure below. This paper covers a study of that orientation, either during the rolling process or by treatment of the finished sheet, in an effort to improve the bend properties and toughness of sheet. Literature The orientation texture of magnesium and magnesium alloy sheet has been studied extensively. Early determinations2 showed that pure magnesium sheet has a preferred orientation in which the basal planes are parallel to the sheet surface within very narrow limits. J. C. hIcDonald3 and J. D. Hanawalt4 reported that sheet containing a small amount of calcium develops a "double" texture, that is, the majority of the basal planes are a few degrees from parallel to the surface and there is a noticeable vacancy at the parallel position. Bakarian5 made careful quantitative pole figures of both pure magnesium sheet and MI alloy SEPTEMBER 1949 sheet which show these features. In all of these studies, however, the orientation was determined by transmission methods in which the resulting pattern is an average through the thickness of the sheet. The tendency of wrought metal to exhibit a different orientation at the surface from that in the center has been reported by many investigators. G. von Vargha and G. Wasserman6 found that with copper, aluminum, iron, and brass the textures of rolled compared to drawn wires were the same at the center but differed markedly at the surface. It was also reported by investigators7 that the orientation of rolled aluminum varies from surface to center. Har-greaves8 found that the surface texture of AM503 (magnesium alloy similar to MI) sheet was different from the center texture. It is reported by Edmunds and Fuller9 that zinc alloy sheet sometimes had a thin layer at the surface with a strong orientation of the basal planes parallel to the surface, which, if present, impaired the bend properties of the sheet. Part1 Surface Orientation ofMag- nesium Alloy Sheet and the Effect on Properties Attempts to correlate the bend properties of magnesium alloy sheet with tension ductility over short gauge lengths proved unsuccessful and the subsequent investigation showed that nonuniformity in orientation is a con- tributing factor as the properties of the surface material have a much more important effect in bending than in tension. A program to study the relationship between surface orientation at the surface and bend properties was then undertaken. First, the effect of etching away the surface of sheet on the bend properties and the orientations at the various depths were studied. Sheet samples of M1, AZ31X, and AZ61X were etched in dilute nitric acid to remove the surface material for various depths to 0.015 in. As may be seen in Table 1, the minimum bend radius improved considerably as the surface layers were etched away but it was necessary to etch the sheet quite deeply, much more so than was found necessary by Edmunds and Fuller9 on zinc sheet. It is also apparent that the amount of etching required is a function of the sheet thickness. In all of this work, radii were measured as R/t, the radius divided by the sheet thickness, in order to eliminate the effect of the reduction in sheet thickness produced by the etching. To determine the orientation texture of the sheet, X ray reflection patterns were taken using copper radiation with the bearn striking the specimen at an angle of 17' to the surface, which is the Bragg angle for the (002) planes of magnesium. Two exposures were made of each specimen, one with the beam perpendicular to the rolling direction and the other with the beam parallel to the rolling direction. The symmetry of the preferred orientation in magnesium sheet is such that these two photographs gave an approximation of the pole figure sufficiently accurate for qualitative work and it was not thought worthwhile to make complete pole figures. These X ray patterns show that the orientation has a much narrower spread at the original surface of the sheet than below the surface. The narrow spread is found in sheet having the majority of the basal planes (002) parallel to the surface, and since this is an unfavorable position for slip, it is