Institute of Metals Division - The Creep Behavior of Heat Treatable Magnesium Base Alloys for Fuel Element Components

The Mg-Zr alloy ZA and Mg-Mn alloy AM503(S) are shown to have a markedly improved resistance to creep deformation after suitable heat treatments. This improvement makes them suitable for certain stress-bearing fuel element components in nuclear reactors. The extent of strengthening is described and an explanation of the behavior of both materials is given, based on a combination of strain-aging and grain growth. The increase in operating temperatures of fuel element components in Calder Hall type nuclear reactors has necessitated the development of magnesium base alloys with a very high resistance to creep at temperatures up to 500°C. Such alloys are not required for fuel element cans, which require high-creep ductility rather than strength, but for can supporting and stabilizing components, which are needed to support the imposed loads without deforming more than about 1 pct in times of up to 40,000 hr. The amount and type of alloying addition made to magnesium for these parts is limited by the necessity of keeping the cross-section to thermal neutrons as low as possible. The alloys must also possess a high resistance to oxidation in CO2. Alloys which have been developed for this application include ZA, an alloy of magnesium with 0.5 to 0.7 pct Zr and AM503(S), an alloy of magnesium with 0.5 to 0.75 pct Mn. In the as-extruded condition these alloys are very weak and ductile in creep but it has been found that they can be strengthened to a significant extent by heat treatment. This paper describes the method of developing a high-creep resistance in ZA and AM503(S), the extent of the strengthening produced and discusses the probable mechanisms of strengthening. TEST MATERIALS Specimens were taken from typical casts of ZA and AM503(S) alloys extruded into 2 1/4-in.-diam bars, supplied by Magnesium Elektron Ltd. Typical analyses of the bars were as follows: The as-extruded mean grain diameter was 0.001 to 0.002 in. for the ZA alloy and 0.003 in. for the AM503(S) alloy. EXPERIMENTAL METHODS Extruded bars of ZA alloy, 2 1/4 in. in diameter and 9 in. long, were heat treated in electrical resistance furnaces in an atmosphere of flowing CO2 containing 50 to 300 ppm water, thereby reducing the extent of oxidation compared with that which would have occurred in air. Heat treatments were carried out at 600oc for times of 8, 24, 48, 72, and 96 hr and material was subsequently both furnace cooled and water quenched. In order to measure the effect of time of heat treatment, specimens were creep tested at 400°C and 336 psi for about 1000 hr. Subsequently, the behavior of material heat treated for 96 hr at 600°C and furnace cooled was tested at a variety of stresses from 200° to 500°C. Tests were also conducted at 200o and 400°C on material in the as-extruded condition for comparative purposes. With the AM503(S) alloy, only the effect of heat treatment at 565°C for 4 hr was examined. It has been shown1 that such a heat treatment produces marked strengthening in this alloy. Tests on this material were conducted at a variety of stresses at 200°, 300°, and 400oc with comparative tests on as-extruded material at 200o and 400°C. The creep tests were carried out on machines using dead-weight loading and direct micrometer strain measurements on specimens 5 in. long and 0.357 in. diameter. At temperatures of 400° C and below, the creep tests were conducted in air, but at higher temperatures an atmosphere of CO2 was used. Grain size measurements were made on ZA in the extruded and heat treated states and on each specimen after creep testing. This was done by a line count of a minimum of 20 grains in two or three random fields in the longitudinal and transverse directions. The same method was used for measuring the grain size of as-extruded AM503(S), but the grain size of the heat treated material was so large that this method could not be employed. For heat-treated AM503(S) the large grained characteristics (between 0.1 and 1 in.) were confirmed by the measurement of individual grains. In the case of the ZA alloy, specimens taken from various stages in the program were analysed for hydrogen by a combustion method. Material in various states was also analysed for the soluble and insoluble zirconium content by dissolving in dilute hydrochloric acid. This technique has been useda for the determination of amounts of zirconium present