Institute of Metals Division - The Effect of Surface Removal on the Plastic Flow Characteristics of Metals Part II: Size Effects, Gold, Zinc and Polycrystalline Aluminum

Studies of the effect of size of the specimen on the change of slopes of Stages I and 11 by surface removal showed that the change of Stage I was independent of size with respect to the polishing rate; however, the change in the slope of Stage 11 with polishing rate increased directly in proportion to the surface area. The removal of the surface during the test affected the plastic deformation characteristics of gold, aluminum, and zinc single crystals and polycrystalline aluminum. The apparent activation energy of aluminum was found to be decreased markedly by removing the surface during the deformation process. In previous papers1-3 it was shown that the surface played an important role in the plastic deformation of metals. By removing the surface layers of a crystal of aluminum by electrolytic polishing during tensile deformation, it was found that the slopes of Stages I, II, and III were decreased and the extents of Stages I and II were increased when the rate of metal removal was increased. By removing a sufficient amount of the surface layer after a specimen had been deformed into the Stage I region, upon reloading, the flow stress was the same as the original critical resolved shear stress and the extent of Stage I was the same as if the specimen had not been deformed previously. The slope of Stage I was decreased 50 pct and that of Stage 11 decreased 25 pct when the rate of metal removal was 50 X 10"5 ipm. These data show that in Stage I the work hardening is controlled almost entirely by the surface conditions, while in Stages 11 and III both surface conditions and internal obstacles to dislocation motion are important. It appears that during the egress of dislocations from the crystal, a fraction of them becomes stuck or trapped in the surface regions and a layer of a high dislocation concentration is formed. This layer would not only impede the motion of dislocations, but would provide a barrier against which dislocations may pile up. In this case, there will be a stress, opposite to that of the applied stress, imposed on the dislocation source and dislocations moving in the region beyond this layer. It has been found convenient to refer to this layer as a "debris" layer. The "debris" layer may be similar to the dislocation tangle observed by thin-film electron microscope techniques.4 Reported in this paper are the results of studies on the effects of removing the surface during plastic deformation on aluminum crystals of various sizes. The effects of the surface on the yield point behavior of gold and high-purity aluminum crystals as well as the creep behavior were also determined. The effects of surface removal on polycrystalline aluminum (1100-0 and 7075-T6) are also reported. EXPERIMENTAL PROCEDURE For those portions of the investigation involving creep and tensile specimens, single crystals, having a 3-in. gage length and a nominal 1/8-in. sq cross section, were prepared by a modified Bridgman technique using a multiple-cavity graphite mold. The single crystals were prepared from materials which had initial purities of 99.997, 99.999, 99.999, and 99.999 pct for Al, Cu, Zn, and Au, respectively. The aluminum specimens for the size effect studies were prepared through the use of a three-tier mold in which crystals having a cross section of 1/8, 1/4, and 1/2 in. were grown from a common seed. The mold design was arranged so that one 1/2-in. crystal, two 1/4-in. crystals, and four 1/8-in, crystals of the same orientation could be cast. With this technique, it was possible to obtain only one set of crystals with the same orientation. Because of this limitation, it was not possible to determine both the changes of extent and slope of the various stages since a large number of crystals of the same orientation would have been required. Instead, only the change of slope as a function of the rate of metal removal was studied by abruptly altering the current density of the electrolytic polishing bath at various strains within the regions of Stages I and 11. The experimental techniques used for the tensile studies were essentially the same as those used previously.1,3 The specimens were deformed in a 200-lb Instron tensile machine, usually at a rate of 10-5 sec-5. A methyl alcohol-nitric acid solution was used as the polishing bath for aluminum. The temperature was maintained constant within ±0.l°C by means of a water bath. The tensile machine was