Institute of Metals Division - The Properties of Sand Cast Mg-Th-Zn-Zr Alloys

The effect of thorium and zinc variations on the strength and 100-hr creep characteristics of Mg-Th-Zn-Zr alloys was investigated. Optimum resistance to creep at 650° and 700°F are attainable within a certain range of thorium and zinc contents. This range does not conform to that which develops maximum tensile properties. RAPID advances have been made during the last few years in the development of magnesium alloys for elevated temperature applications demanding high resistance to creep. The beneficial effect of rare-earth metals on the creep resistance of magnesium alloys has been emphasized by a number of publications1-13 and such alloys are now in commercial production. The use of thorium as an alloying ingredient in magnesium was mentioned by McDonald and also in two Alien Property Custodian patent applications.10,17 The initial observation of Sauerwald that thorium contributes still higher creep resistance to magnesium than is attainable with rare-earth metals has recently been substantiated.'" " In fact, it has been demonstrated that the useful temperature range of magnesium alloys is appreciably extended by the use of thorium. In all cases, it was observed that zirconium must be included in the alloys in order to render them fine grained and more readily castable. Several recent publications:2-27 indicate that a still further improvement in creep resistance and a further extension of the useful temperature range can be realized by the addition of zinc to alloys. The primary purpose of this paper is to present the results of a comprehensive study of the effect of zinc on the strength and creep characteristics of Mg-Th-Zr alloys. Compositions covering the range of thorium content from M to 6 pct and zinc content from 0 to 5 pct have been investigated. The creep characteristics at 650" and 700°F reported in this paper are based on results of tests of 100-hr duration. It is appreciated that creep tests of 100-hr duration might not yield adequate data for design purposes for parts with much longer expected life. However, for the purposes of the present discussion, it is felt that the combination of stresses and temperatures used in the 100-hr creep tests have yielded a clear representation of the compositional variation of creep resistance at the temperatures investigated. Creep tests of 1000-hr duration are now in progress on a few of the most promising alloys. Preparation and Testing of Alloys The alloys studied in this intensive investigation were prepared in 25 lb capacity mild steel crucibles. The thorium, zinc, and zirconium were alloyed and poured as described in earlier publications The thorium was introduced into the melt in the form of a Mg-Th hardener," the zinc added in the metallic form, and the zirconium alloyed in the form of the commercial hardener containing magnesium and 30 to 50 pct Zr.10, 26 Fluxing practices for melting and refining were the same as for magnesium-rare-earth metal-zirconium alloys. The melts were sampled for analytical determinations and poured into separately cast 1/2 in. diameter standard tensile bars. The test bars were given a precipitation treatment of 16 hr at 600°F in laboratory furnaces. It has been shown by other tests that a high temperature solution treatment followed by an aging treatment is unnecessary for the development of optimum properties in Mg-Th-Zn-Zr alloys. The selection of 600°F as the aging temperature was based on an attempt to achieve metallurgical stability without coalescence of the undissolved phases and the attendant loss in strength. The thorium, zinc, and zirconium contents of each melt were determined chemically. The zirconium contents are reported in two parts, "soluble" and "insoluble," referring, respectively, to the portions present in the alloy which are soluble and insoluble in dilute HCl acid. Distinction is being made between these two components of the zirconium content in the alloys because it has been found that only that portion of the zirconium content which is soluble in dilute inorganic acids affects the structure and properties of the alloys. The usual impurities consisting of copper, iron, manganese, and nickel were determined spectroscopically. The analysis for each melt is listed in Table I. A description of the methods of tension and creep testing has been detailed in earlier papers. The tests were performed with the cast skin re-