Institute of Metals Division - The Tantalum- Zirconium Alloy System

The phase diagram of the Ta-Zr system is presented with a discussion of the methods used in its determination. The solidus contains a minimum at 1820°C near 25 wt pet Ta. A complete solid solution exists at elevated temperatures between tantalum and ß zirconium. This solid solution decomposes monotectoidally at 800°C and 12 wt pet Ta. The maximum solubility of tantalum in a zirconium is slightly less than 2 wt pet, and decreases with decreasing temperature. The solubility of zirconium in tantalum is 5 wt pet at the monotectoid temperature and about 2 wt pet at room temperature. THIS investigation was part of a program of research on refractory metal alloy systems having potential application in nuclear reactor technology. Preliminary prop-ess has been reported in the Ames Laboratory annual research reports.l Most of the previously reported work on the Ta-Zr alloy system consisted of partial phase diagram investigations and the determination of the mechanical properties of the zirconium-rich alloys. Anderson eta1.2 studied alloys containing up to 30 wt pet Ta as part of an investigation of several zirconium alloy systems. These investigators also determined some of the mechanical properties of the alloys at room temperature and 650°C. In a discussion of Anderson's work, Pfei13 suggested that the bright phase in the microstructures of the intermediate alloys is a tantalum-rich solid solution or an intermediate phase in a matrix of ß zirconium solid solution. Litton,4 Keeler,5 and Chubb6 determined the mechanical properties of zirconium-rich alloys at ambient and elevated temperatures. Van Thyne and McPherson7 reported the tensile properties