Institute of Metals Division - The Texture and Mechanical Properties of Iron Wire Recrystallized in a Magnetic Field

Swaged iron wire has a cylindrical {001} <110> texture. The texture is also cylindrical after re-crystallization in the absence of a magnetic field, but <111> and <112> components are added to this texture when recrystallization occurs in a field. The mecizanical properties in tension and in torsion are not greatly altered by these changes in texture. AS shown in a previous paper,1 cold-worked wires of the two fcc metals copper and aluminum can be made relatively strong in torsion and weak in tension, or vice versa, by proper control of preferred orientation (texture). The deformation texture can be controlled by selection of the starting texture (texture before deformation), because certain initial orientations are stable during deformation. The present paper reports on similar work performed on bcc iron. In this case it was clear at the outset that there was no hope of controlling the deformation texture, which is one in which <110> directions are aligned parallel to the wire axis. (1t has usually been regarded as a fiber texture, but Leber2 has recently shown that it is a cylindrical texture of the type {001} <110>. In either case, <110> directions are parallel to the wire axis.) There is general agreement on this texture among a large number of investigators, which in itself suggests that the starting texture has no influence on the deformation texture. More direct evidence was produced by Barrett and Levenson,3 who reported that iron single crystals of widely varying initial orientations all had a single <110> texture when cold-worked into wire. Thus <110> is a truly stable end orientation for iron and probably for other bcc metals as well. Under these circumstances attention was directed to the possibility of controlling the recrystallization texture. This texture is normally <110> in iron,4 just like the deformation texture. However, it is conceivable that this texture could be modified by a proper choice of the time, the temperature, and what might loosely be called the "environment" of the recrystallization heat treatment. In the present work the environmental factor studied was a magnetic field. The effect of heating in a magnetic field ("magnetic annealing") on recrystallization texture has been investigated by Smoluchowski and Turner.5 They found that a magnetic field produced certain changes in the recrystallization texture of a cold-rolled Fe-Co alloy. The texture of this material is normally a mixture of three components, and the effect of the field was to increase the amount of one component at the expense of the other two. Smoluchowski and Turner concluded that the effect was due to magnetostriction. With the applied field parallel to the rolling direction, the observed effect was an increase in the amount of the texture component which had <110> parallel to the rolling direction. In the Fe-Co alloy they studied, the magnetostriction is low in the <110> direction and high in the <100> direction. Thus nuclei oriented with <110> parallel to the rolling direction will have less strain energy than those with <100> orientations and will therefore be more likely to grow. In a later paper on the same subject, Sawyer and Smoluchowski6 ascribed the effect to magneto-crystalline anisotropy and made no mention of magnetostriction. In the papers of Smoluchowski et al. the intensity of the magnetic field was not reported but it was presumably large, inasmuch as it was produced by an electromagnet. In the second paper6 it is specifically mentioned that the specimens were magnetically saturated. But if magnetostriction has a selective action on the genesis of stable nuclei during recrystallization, that selectivity must depend only on differences in magneto-strictive strains between different crystal orientations and not on the absolute values of those strains. Thus the saturated state does not necessarily produce the greatest selectivity, because the relative difference in magnetostrictive strains between different crystal directions may be larger for partially magnetized crystals than for fully saturated ones.7 In the present work the specimens were subjected to relatively weak fields (0 to 100 oe) produced by solenoids. MATERIALS AND METHODS Armco ingot iron rod (containing 0.02 pct C and 0.19 pct other impurities) was swaged from 0.25 in. in diam. to 0.05 in., a reduction in area of 96 pct. The mechanical properties in tension and torsion were measured as described previously.&apos; Textures were measured quantitatively with chromium or iron radiation and an X-ray diffractometer,8,1 and