Institute of Metals Division - The Thermal Expansion of Nb3Sn(Cb3Sn)

The lattice parameter of the inlerrnetallic compound Nb3Sn has been measured as a function of temperature from 80° to 1290°K. The results are compared with published data on the thermal ex- ThE recent interest in the intermetallic compound, Nb3Sn, as an engineering material for the production of superconducting devices has necessitated that certain engineering data be obtained. Because of the difficulty encountered in producing bulk pansion of niobium and indicate that the compound when made by diffusion of tin into niobium at 1000°C, would be subjected to a tensile strain of about 0.1 pct when cooled to room temperature. material which is single phase, the coefficient of thermal expansion has not been measured by dilata-tional methods. Therefore the lattice parameters of fine-grained samples of Nb3Sn produced on the surface of a niobium sheet by heating in molten tin at 950°C have been obtained as a function of temperature. The results are compared with published data on niobium2 and Nb3Sn3 and with lattice-parameter measurements made on small single crystals of Nb3Sn.