Institute of Metals Division - Transformation in Cobalt-Nickel Alloys

TO reach equilibrium between different phases in cobalt-rich alloys requires prohibitively long annealing cobalt-richalloystimes when temperatures are below about 700°C. The fact that a transformation from face-centered cubic to close-packed hexagonal readily tered takes place at temperatures below this in the cobalt-rich solid solutions is not an indication that thermally activated processes occur at an appreciable rate, for the transformation is well established as martensitic in nature. Wide divergence between heating and cooling experiments and high sensitivity to prior heat treatment make it difficult to judge temperatures of equilibrium between the phases.&apos; One object of the present work was to see if the information object of on the relative stability of phases could be gained by substituting plastic deformation for thermal agitation. Procedures were worked out that led to the determination of a diffusionless type of phase diagram, which represents the temperature of of phase equal stability for phases of the same composition, and the technique was applied to the Co-Ni system. Another object of the work was to see whether or not deformation would generate frequent stacking faults when these were thin lamellae of quentstackingfaultsa phase having higher free energy than the parent phase. The alloys were prepared in 80 to 100 g melts from cobalt (with metallic impurities estimated spectrochemically as follows: Ni, 0.05 pct; Fe, 0.001 pct.; Mg, Si, Cu, Cr, Al, < 0.001 pct) and Mond Car-bony1 nickel (with Fe, 0.05 pct; Si, 0.003 pct; C, 0.61 pct.; Cu, 0.001 pct; Co, Cr not detected, < 0.01 pct). The metals were melted in pure Al2O3 crucibles. An atmosphere of argon, that had been purified by passing over hot magnesium chips, was used for the alloys that, by analysis of the portions of the ingots actually used, were found to contain 15.3, 25.7, and 35.0 pct Ni, and vacuum melting (after degassing) was used for those containing 29.4 and 31.5 pct Ni. After induction melting the alloys were allowed to solidify in the crucible, and slices % in. thick x ½ in. in diam were annealed 12 hr at 1350°C for homogenization. These same specimens were used throughout the series of experiments, with annealing treatments of 4 hr at 900°C in purified hydrogen followed by furnace cooling, alternating with the deformation and X-ray tests discussed below. Results Spontaneous transformation was observed on cooling to room temperature in all alloys containing 29.4 pct Ni or less and by cooling the 31.5 pct alloy to — 195°C but was not observed in the 35 pct alloys after cooling to —195°C. These results are in satisfactory agreement with the cooling experiments of Masimoto.4 From these data it is clear that the temperature of beginning transformation M,,, drops to 20°C with the addition of about 30 pct Ni. The test for spontaneous transformation was metallographic. Specimens were thermally polished by annealing 10 hr in hydrogen at 1350°C, then furnace cooled; if trans- formation had occurred there were relief effects visible on the thermally polished surfaces. These markings were narrow straight lines, usually resolvable at high magnification as clusters of fine lines that resembled slip lines. It was concluded that they resulted from displacements on (111) planes, for the number of directions in individual grains often reached but never exceeded four, and lines could always be found parallel to the thermally etched (111) boundaries of annealing twins. The markings were thus consistent with the idea that the transformation occurs by (111) plane displacements (Shockley partial dislocations moving on (111) planes). This was further confirmed by X-ray tests for stacking disorders. Using an oscillating crystal technique previously employed to detect strain-induced faulting in Cu-Si alloys," streaks indicative of the stacking faults were looked for and found on X-ray films of the spontaneously transformed 25.7 pct Ni alloys, as expected by analogy with Edwards and Lipson&apos;s results on pure cobalt." The streaks were much intensified after rolling at room temperature. Transformation induced by plastic strain was investigated as a function of alloy composition and temperature of deformation. A series of tests was made to determine suitable straining and X-raying techniques. Filing was found inferior to abrasion in converting cubic samples to hexagonal, and abrasion was less effective than peening in producing smooth unspotty Debye rings in the X-ray patterns. Because the diffraction lines were broad, Geiger-counter spectrometer records of filings were less sensitive in revealing small amounts of transformed material than X-ray patterns recorded on films in a small diameter camera. After these exploratory tests the following methods were adopted. Specimens that had been annealed at least 4 hr at 900°C and furnace cooled were mounted in a block of aluminum, brought to temperature, and peened thoroughly with a mullite pestle preheated to the same temperature. The specimens were then quenched to room temperature. In peening, a circular area of % in. diam was given 500 blows. A few control tests showed that an additional 1000 blows did not detectably change the proportions of the phases present. The amount of transformation was judged by X-ray reflection patterns from the peened surface, using the innermost four lines of the cubic and the hexagonal patterns with filtered CoKa radiation,