Interfacial Phenomena And Reaction Kinetics Between Carbon And Slag Containing MnO

Wettability of graphite by synthetic SiO2-Al2O3-CaO-MnO slags with varied MnO content and by industrial slags was studied at 1350-1600 °C using sessile drop method under argon atmosphere. Initial contact angle was the lowest (110-115o) for the MnO-free slag. For slags with 10-40 wt% MnO, the initial contact angle was in the range 125-135o. The contact angle decreased with the contact time. The change in the contact angle with slag mass was found insignificant. The surface tension of slags obtained from the drop shape analyses was 500-800 mN/m and varied in a narrow range with temperature and MnO concentration. The reduction rate increased with increasing MnO content in the synthetic slag from 20 wt% to 40wt% and temperature. Increasing temperature also increased the rate of reduction. No correlation was observed between the reduction rate and MnO content in the synthetic slags in the range 0-20 wt% and in the industrial slags. The rate of SiO2 reduction from the molten slag was close to the rate of MnO reduction. The MnO-free slag had the largest contact area with graphite substrate. Keywords: reduction, wettability, graphite, slag, manganese, surface tension.