Iron and Steel Division - A Thermodynamic Study of the Reaction CaS + H2O [=] CaO + H2S and the Desulphurization of Liquid Metals with Lime

THE desulphurization of molten iron and steel is a very complicated process. One way to arrive at a better understanding of this process is to break it down into several simpler chemical processes that can be studied individually in the laboratory. For a study of the different factors that influence the equilibrium distribution of sulphur between liquid metals and slags, several simpler equilibria may be investigated. One very important subject is the determination of the escaping tendency of sulphur in the liquid metal and its dependency on temperature and composition of the melt. Several papers in this field have recently been published.', ' Another subject is the study of the sulphur capacity of the slag. A molten slag is indeed complex, and even if sulphur distribution data for a large variety of molten slags may give empirical data about their desulphurizing power, the importance of the individual components is still not quite clear. It is accepted generally that lime is the most important desulphurizing component in the slag. The present investigation has as its purpose to study the desulphurizing power of lime in its standard state, and to provide a basis for thermodynamic calculations of the desulphurizing power of various lime-containing slags. The standard state of lime at steelmaking temperatures is solid calcium oxide, CaO. It can react with sulphur to form solid calcium sulphide, CaS. The relative stability of calcium oxide and calcium sulphide is expressed by the free energy of the reaction: 2Ca0 (s) + S1 (g) = 2CaS (s) + O2 (g) The existing free energy data for this reaction, listed by Kelley5 nd Osborn,' are uncertain to about 10 kcal and are of limited value for a calculation of equilibrium constants. Under the conditions prevailing in a melting furnace, the sulphur pressure may be expressed conveniently by the ratio H,S/H2 and the oxygen pressure by the ratio H,O/H, (or CO,/CO). The desulphurizing power of calcium oxide may, therefore, be studied by the reaction CaO + HIS = CaS + H2O. A study of this reaction may be complicated by certain side reactions: Water vapor and hydrogen sulphide may react. to form sulphur dioxide, and calcium sulphide may be oxidized to calcium sulphate. A thermodynamic calculation shows that these side reactions will be suppressed to insignificance if the equilibrium is studied in the presence of an excess of hydrogen. The apparatus used is shown in Fig. 1. About 10 g calcium oxide and 20 g calcium sulphide (laboratory qualities) were intimately mixed, and some water was added to make a thick paste. The paste was put into a thimble of zirconium silicate, which was placed within the constant temperature zone of a furnace, and capillary refractory tubes were attached in both ends. After the mixture had been heated in dry hydrogen at 1000°C for several hours all Ca(OH), and CaCO, had decomposed and CaSO, was reduced, so only CaO and CaS remained in the thimble forming a porous plug. The mixture was examined by X-ray diffraction after the initial reduction in dry hydrogen as well as after the subsequent experimental runs up to 1425 °C. It was shown that crystalline calcium oxide and calcium sulphide were always present together in about equal amounts. The unit cell edges were found to be 4.80A for CaO and 5.68A for CaS in good agreement with existing literature values." This shows that the mutual solid solubility is very small, and that the compounds are present in their standard states. Purified hydrogen was passed through water sat-urators kept at constant temperature in a thermostat bath. The amount of water vapor saturation was checked by means of a dew point method, not shown on Fig. 1. The gas mixture was passed through the capillary inlet into the furnace, where it was sifted through the porous plug of calcium oxide and calcium sulphide. The hydrogen sulphide present in the outgoing gas was absorbed in a zinc acetate solution and the hydrogen was collected over water. When one liter of hydrogen had been collected, the amount of hydrogen sulphide was determined by iodometric titration. As one molecule of H,O is used for the formation of each molecule of H,S, the equilibrium ratio H,S/H,O would be , where (H,O) is the molar concentration in the ingoing gas, and (H,S) the molar concentration in the outgoing gas. In the present work (H,S) was always very small compared to (H20). In order for the observed H,S/H20 ratio to represent the true equilibrium ratio the gas flow has to be: 1—Sufficiently slow to give a complete establishment of equilibrium, and 2—sufficiently fast to counteract thermal diffusion. Incomplete reaction would give a value decreasing with increasing flow rate, and thermal diffusion would give a value increasing with decreasing flow rate. When inlet and outlet tubes of about 2 sq mm cross-section were used, the observed gas ratio was independent of the flow rate between 15 and 125 cc per min, Fig. 2. In this range, therefore, the observed gas ratio represents true equilibrium.* For the rest of the in-