Iron and Steel Division - Activities of Manganese Oxide, Sulfide Capacities and Activity Coefficients in Aluminate and Silicate Melts

Manganese oxide acitivities and sulfide capacities have been measured at 1650°C in mixtures of MnO + A1203 and MnO + SiO2 - Al2O3. Sulfide capacities have also been measured at 165O0C for melts of MnO + SiO2, MgO + SiO2, MgO + SiO2 + Al2O3, MgO + MnO + SiO2, and SiO2 + Al2O3 and for crystalline CaO. The activity coefficients of the sulfides of manganese and magnesium have been derived where possible. It looks as though the activity coefficients of sulfides are greatest at compositions where the free energies of formation of the silicate mixtures have their maximum negative values. The amphoteric nature of alumina is reflected in the results for the binaries and ternaries in which it is present with silica. The limiting solubility of CaS in CaO at 1650°C is 6.3 x 10-4 mole fraction. THE activities of manganese oxide have been measured in a variety of silicate and aluminate melts by use of the equilibrium (MnO)slag = [Mn]pt .½O2 [l] and the experimental techniques described previously.' Sulfide capacities (CS = wt pct S (PO2/PS2)½) have also been determined in a series of melts, by use of an established method2 which exploits the equilibrium (O°) + ½S2 = (S") . ½O2 [2] If CS and the activity of a metal oxide are known in a melt, the activity coefficient of the metal sulfide can be calculated by use of the equilibrium constant K, for the pure phase reaction MO i ½S2 = MS + ½O2 [3] The activity coefficient of the sulfide is then given by the equation