Iron and Steel Division - Activity of Carbon in Liquid-Iron Alloys

The effects of various elements on the activity coefficient of carbon in liquid iron have been studied by two experimental methods: 1) equilibration with controlled mixtures of CO and CO2; 2) the solubility of graphite in the melt. Activity coefficient of C is increased by Al, Co, Cu, Ni, P, Si, S, and Srz. It is decreased by Cr, Cb, Mn, Mo, W, and V. THE thermodynamic properties of the iron-carbon binary system have now been fairly well established, although some uncertainty remains with respect to the exact location of some of the phase boundaries. The activity of carbon in ferrite and in austenite has been measured in the classic researches of R. P. smith' while similar measurements by Richardson and ~ennis, and by Rist and chipman3 have established the values of the activity of carbon in liquid iron up to 1760°C. On the other hand, our knowledge of the effects of alloying elements on the activity of carbon in dilute solutions is restricted to Smith's experiments on systems Fe-C-Mn and Fe-C-Si in the austenitic range and to some more recent experiments of schwarzman4 in the a range. In addition there have been a number of determinations of the effects of various elements on the solubility of graphite in liquid iron, and from these the corresponding effect in saturated solution may be obtained. The purpose of the present study was to extend the investigation of the liquid system to include the effects of alloying elements upon the activity coefficient of carbon, principally in dilute solutions. Equilibrium measurements were made on the reaction C + co, = 2 CO (g) The prepared mixture of CO and CO,, diluted with argon, flowed over the surface of the liquid metal which, after several hours' exposure to the gas, was quenched and anqlyzed. As in the earlier experiments, the principal experimental difficulty was in the deposition of carbon on the parts of the furnace at temperatures slightly below that of the metal bath. In order to minimize this difficulty, the ratio (Pco)2 /PCo2 was restricted to values not much higher than 100 atm, and correspondingly the carbon concentration in the metal seldom exceeded 0.30 pct. EXPERIMENTAL METHODS The method and apparatus were essentially the same as used by Rist and Chipman.3 The gaseous mixture consisting of highly purified CO, CO,, and argon, each controlled by a flowmeter, was led into the furnace and passed over the surface of the liquid-iron melt which was heated and stirred by high-frequency induction. One slight modification was made in that a molybdenum susceptor was placed outside the crucible for the sake of uniformity of temperature and to combat the tendency of carbon to precipitate on the crucible wall. Pure alumina crucibles approximately 25 mm ID were used. The charge consisting of about 30 g was made up of electrolytic iron, the alloying element to be added, and enough graphite to supply slightly more or less than the anticipated equilibrium carbon concentration. All metals used were of high purity. Metallic chromium, columbium, and vanadium were from special lots supplied by the Electro Metallurgical Co. Tin, copper, molybdenum, tungsten, cobalt, and nickel were of purest commercial grades. The electrolytic iron, after being cut to the proper size for charging, was prereduced by hydrogen at 850° to 1000°C to remove surface oxidation. The oxygen content of the reduced material was 0.002 pct. This treatment made it easy to control the carbon content of the initial melt. The charge was melted under the gas mixture to be used for the entire run. In some earlier melts the charge was melted under a stream of argon, but in this case some alumina was reduced from the crucible, and the aluminum thus absorbed in the melt was subsequently oxidized with the formation of a solid film of alumina on the surface of the melt. AS another safeguard against film formation, overheating of the bath was carefully avoided. All runs were made at a temperature of 1560°C. Under experimental conditions a charge of pure iron picked up 0.17 pct C in 3 hr and 0.23 pct C in 6 hr under an atmosphere for which the equilibrium concentration of carbon is 0.27. It is clear that the time required to reach equilibrium from an initially carbon-free melt would be very great. For this reason each experiment was started with a melt of known carbon concentration not far above or below the expected equilibrium value, and each melt was held at temperature for a period of at least 5 hr. Under such circumstances it was possible to chart the approach to equilibrium from both high-carbon and low-carbon materials. Temperature was controlled by frequent optical observation and adjustment and the metls were timed in such a way that the final 2 hr occurred during a time when electric power was steady; for example, 2 to 4 pm or after 11 pm. In melts containine volatile metals such as copper, tin, and mangane\e the time of holding was decreased somewhat in