Iron and Steel Division - Activity of Silica in CaO-Al2O3 Slags at 1600° and 1700°C

New data on the distribution of silicon between slag and carbon-saturated iron at 1600oand 1700oC are presented which, in combination with previously published data, permit the determination of silica activities over a broad range of compositions in the CaO-Al2O3-SiO2 system. The distribution of silicon between graphite-saturated Fe-Si-C alloys and blast furnace-type slags in equilibrium with CO has been described in previous publications.1"3 In this past work the silica-silicon relation was established at temperatures of 1425" to 1700°C for slags containing up to 20 pct Al2O3. This paper presents the results of additional studies at 1600" and 1700° C which extend the silicon distribution data at these temperatures for CaO-A1203-SiO2 slags over a range from zero pct A12O3 to saturation with A12O3, or CaO.2A12O3. The upper limit of SiO, is set by the occurrence of Sic as a stable phase when the metal contains 23.0 or 23.7 pct Si at 1600" or 1700°C, respectively. The activity of silica over the expanded range is determined directly from the distribution data.3 Recently, 4-7 other investigators have studied the activities of SiO, and CaO, principally in the binary system, using different methods and obtaining somewhat different results. EXPERIMENTAL STUDY The experimental apparatus and procedure have been fully described in previous publications.1, 3 Six new series of experimental heats have been made, four at 1600° and two at 1700°C. Master slags of several fixed CaO/A12O3 ratios were pre-melted in graphite crucibles, and these were used with additions of silica to prepare the initial slag for each experiment. Slag and metal were stirred at 100 rpm and CO was passed through the furnace at 150 cc per min. The initial sample was taken 1 hr after addition of slag at 1600°C or 1/2 hr after addition at 1700°C. The run was normally continued for 8 hr at 1600°C or 7 hr at 1700°C, and the final sample was taken at the end of this period. Changes in Si and SiO2 content indicate the direction of approach to equilibrium, and in a series of runs where the approach is from both sides this permits approximate location of the equilibrium line. Fig. 1 shows the results of such a series of 15 runs at 1600°C for slags of CaO/Al2O3 = 1.50 by weight. Figs. 2 and 3 record other series at 1600°C and Fig. 5 a series at 1700°C with fixed CaO/Al2O3 ratios. The results of the experiments at 162003°C have been reported in part in a preliminary note.3 In the experiments recorded in Figs. 4 and 6, the slags were saturated with A12O3 (or with CaO.2A12O3 within its field of stability) by suspending a pure alumina tube in the melt during the course of the run. The final slag analyses were used to establish the liquidus boundaries8 in the stability fields of CaO.2Al,O3 and of A120,. ACTIVITY OF SILICA The free-energy change in the reaction has been calculated by Fulton and chipman2 from recent and trustworthy data including heats of formation, entropies, and heat capacities. The more recent determination by Olette of the high-temperature enthalpy of liquid silicon is in satisfactory agreement with the values used and therefore requires no revision of the result which is expressed in the equation: SiO, (crist) + 2C (graph) = Si + 2CO(g.) [1] &F° = + 161,500 - 87.4T The standard state for silica is taken as pure cristobalite and that of Si as the pure liquid metal. Since the melts were made under 1 atm of CO and were graphite-saturated, the equilibrium constant for Eq. [I] reduces to K1 = asi /asio2 The value of this constant is 1.77 at 1600°C and 16.2 at 1700°C. Through K1, the activity of silica in the slag is directly related to the activity of silicon in the equilibrium metal.