Iron and Steel Division - Evaluation of pH Measurements with Regard to the Basicity of Metallurgical Slag

The correlation of the high temperature chemical properties of slag-metal systems with some easily measured property of either slag or metal at room temperature has been the goal of both process metallurgists and melting operators for many years. There are several rapid methods for estimating various constituents in steel in addition to the conventional chemical methods which are quite fast, but these do not reveal the nature of the slag as a refining agent, which is of primary interest to the steelmaker. Furthermore, there are several methods for examining slag, the three principal ones being slag pancake, petrographic examination, and the previously mentioned chemical analysis. The main objection to the last two is the lime required to make a satisfactory estimate of the mineralogical or chemical components. The objection to the first is the inadequacy of the information obtained. A new technique has been developed by Philbrook, Jolly and Henry1 whereby the properties of slags are evaluated from an aqueous solution leached from a finely divided sample of slag. It is known that the pH or hydrogen ion concentration (of saturated solutions that have dissolved certain basic oxides, notably calcium oxide) will indicate a pronounced basicity. Philbrook, Jolly and Henry devised the pH measurement technique in order to supply open hearth operators with a fast, reasonably accurate method of estimating slag basicity. They offered the method as an empirical observation and made no claims as to its theoretical justification. The results were presented as an experi-metally observed relationship which applied over an important range of basic open hearth slags. They found that, in plotting the measured pH against the basicity, the best relationship existed between the pH and the log of the simple V ratio, CaO/SiO2. Extensive investigation also showed that there were several variables in the experimental technique that influenced the results and necessitated following a standard procedure to obtain reproducible pH readings. These variables were: 1. Particle size of the slag powder used. 2. Weight of sample used per given volume of water. 3. Time of shaking and standing allowed before the pH was measured. 4. Exclusion of free access of atmospheric carbon dioxide to the suspension. 5. Temperature of the extract at the time the pH was measured. In subsequent investigations of the pH method by Tenenbaum and Brown2 and by Smith, Monaghan and Hay3 the general conclusions of Philbrook's work were reaffirmed. It was the object of the present investigation to extend the technique to a point where it could be used to evaluate slags of all types. Experimental Results PARTICLE SIZK OF SLAG POWDER A large sample of commercial blast furnace slag of intermediate basicity (V-ratio 1.15) was selected for the study. The slag had been put through a jaw crusher until all of it passed through a 20 mesh screen. Five fractions of this crushed material were separated, -20 to +40, -40 to +60, -60 to +100, -100 to +200, and -200 mesh. A representative sample of 0.5 g was removed from each fraction and the pH determined using the method of Philbrook. Check pH analyses on the sample fractions varied due to the different amounts of shaking. To eliminate this variable, a mechanical shaker was employed. In order to know the exact time of contact between the slag and water, it was found necessary to filter the extract at the end of the shaking period. Using the mechanical shaker and a filtering apparatus, similar runs were made on the five fractions for contact times of 5, 10, 20, and 40 min. Random checks gave reproducible results within 0.02 pH. The data are plotted in Fig 1. It can be seen from the plot that each slag fraction is hydrolyzed to an extent that is roughly proportional to the surface area exposed to the water. The (—100 to +200) mesh material changed very little in pH after 10 min. shaking time. The curves are symmetrical and lie in proper relation to one another. The —200 mesh curve appears to be somewhat flatter than the others, but this can be attributed to the portion of very fine material that is not present in the other fractions. The closeness of the (-100 to +200) mesh curve to the —200 mesh curve and the fact that a —100 mesh sample would contain amounts of slag down to 1 or 2 microns in diam were considered sufficient reasons for selecting a —100 mesh sample as representative of the whole sample of slag for the purposes of this investigation.