Iron and Steel Division - Ionic Nature of Liquid Iron-Silicate Slags

Measurements of current efficiency on iron-silicate slags in iron crucibles showed that conduction is about 10 pct ionic in slags with less than 10 pct silica and about 90 pct ionic in slags with more than 34 pct silica, increasing linearly in the intermediate range. The balance of the conduction is electronic in character. Silicate ions are discharged at the anode with the evolution of gaseous oxygen. Transport experiments show that the ionic current is carried almost entirely by ferrous ions, which may be assigned a transport number of one. THERE has been increased evidence in recent years that the constitution of liquid-oxide systems (slags) is ionic.1-3 The principal studies designed to establish the structure of liquid slags have been by electrochemical methods', " and conductivity measurements1,6,7 which also have indicated the presence of semiconduction in several silicate systems1,4-0 and in pure iron oxide.' It is well known that many slag-forming metallic oxides have an ionic lattice type in the solid state, and their properties are determined to a large extent by the lattice defects and ion sizes. As Richardson8 as pointed out, the detailed models of liquid slags cannot be found on thermodynamic data only but "must rest on a proper foundation of compatible structural and thermodynamic knowledge, combined by statistical mechanics." A careful thermodynamic study of the iron-silicate slags has been carried out by Schuhmann with Ensio9 and with Michal.10 They obtained experimental data relating equilibrium CO2: CO ratios to slag composition and made thermodynamic calculations of the activities of FeO and SiO, and of the partial molal heats of solution of FeO and SiO2 in the slags. It was found that the activity-composition relationships deviate considerably from those to be expected from an ideal binary solution of FeO and SiO2. However, the partial molal heat of solution of FeO into the slags was estimated to be zero. Their experimental results were correlated with the constitution diagram for FeO-SiO2 of Bowen and Schairer,11 with the results of Darken and Gurry" on the Fe-O system, and with the work of Darken"' on the Fe-Si-O system. All these studies were found to be consistent with one another. The variation of the mechanism of conduction with composition in the liquid iron-oxide-silica system in the range from pure iron oxide to silica saturation (42 pct SiO2) in iron crucibles was reported in a preliminary note." The current efficiency, or conformance to Faraday's law, showed some ionic conductance at all compositions, the proportion increasing with the concentration of silica. The current-efficiency experiments since have been extended. Furthermore, transport-number measurements have been completed in silica-saturated iron silicates to determine the nature of the conducting ions. Experimental Current Efficiency in Liquid Iron Oxide and Iron Silicates using Iron Anodes: This study was carried out by passing direct current through slags in the range from pure iron oxide to iron oxide saturated with silica (42 pct silica), using pure iron rods as anodes and the iron container as the cathode. A copper coulometer was included in the circuit to indicate the quantity of current passed during electrolysis. Assuming that the cation involved is Fe-+, the theoretical quantity of iron lost from the anode according to Faraday's law may be calculated and when compared with the actual loss observed, gives an indication of the extent to which Faraday's law has been obeyed. It also gives an indication of the presence and extent of ionic conduction in the melt. Preparation of the Slags: About 100 g of chemically pure Fe,O, powder is placed in an iron pot which is heated by induction until the contents liquefy. In this way, FeO is produced according to the reaction Fe2O3 + Fe = 3 FeO. More Fe2O3 or SiO, powder is added and, when a sufficient quantity of molten slag is obtained, the induction unit is turned off, the pot withdrawn, and the molten slag poured on to an iron plate. Homogenization and Electrolysis of the Slag: Apparatus—After considerable development, the setup illustrated in Fig. 1 proved to be quite satisfactory. A is an Armco iron cylinder, 1 in. ID and 1/8 in. wall, consisting of three sections placed one on top of the other. The bottom section is a pot about 5 in. long with a small hole drilled in its bottom to allow withdrawal of gases during evacuation of the apparatus. The middle section is 6 in. long and consists of a pot which serves as the slag container, while the top section is a hollow-cylinder continuation of the slag-container pot. The height of this latter section is about 5 in., giving an overall length of approximately 16 in. The iron cylinder is constructed in this way for ease of fabrication, the individual sections becoming welded together after the