Iron and Steel Division - Microstructures of Magnesiowüstite [(Mg, Fe)O] in the Presence of SiO2

Periclase-type oxides were examined microscopically after being exposed to siliceous liquids. The rate of grain growth was found to be inversely proportional to the grain diameter. Grain growth proceeds more rapidly at higher temperatures, but is retarded by increasing liquid contents. aMag-nesiowiistites with higher MgO contents grow less rapidly than those with higher FeO contents. The growth rate is reduced by the presence of a second solid phase. The silica-containing liquid penetrates as a film between the individual magnesiowus tite grains. This is independent of time, temperature, amount of liquid, or the MgO/ Fe0 ratio. When present, olivine and spinel-type phases can provide a solid-to-solid &apos;&apos;bridge" between magnesioustite grains. THIS paper presents the results of a study of the microstructures of periclase type oxides in the presence of a silicate liquid. The purpose was to learn more about the effect of service factors such as 1) time, 2) temperature, and 3) liquid content upon A) grain growth, and B) liquid location among the solid grains. This study was prompted by the fact that periclase refractories are known to have very little solid-to-solid contact when the phases which are present are limited to periclase and liquid. Such a micro-structure gains industrial significance because it permits fracture during service when stresses are applied at high temperatures. The details of ceramic microstructures have not received extensive attention. This is in contrast to the extensive attention given to a) the phase relationships pertaining to refractory compositions, and b) the details of the microstructures of comparable metallic materials. A brief review will be made of the pertinent phase relationships and microstructural considerations in general, as well as of refractory compositions. a) Phase Relationships. This investigation was limited to those compositions in which (Mg, Fe)O was the solid phase. MgO and FeO form a complete series of solid solutions. Pure MgO has the name of periclase. The related FeO structure is called wustite. Both have the NaC1-type structure: however, wustite possesses a cation deficiency so that the true composition is Fe<10 even in the presence of metallic iron. The phase relationships involving solid (Mg, Fe)O and a silicate liquid are shown in Fig. 1. In this case. the liquid is saturated with (Mg, Fe)o. There-fore its SiOz content is below that encountered in orthosilicate liquids. As a consequence the liquid phase specie:; are primarily the following ions: and 0-&apos; plus occasional Fe+ ions. Two features are of importance: a) the liquid contains relatively small species and b) the liquid contains large quantities of the same species as the solid. viz., Fig. 2 shows the system, FeO-SiOz, which will be used in some of the discussions that follow. This diagram is the right side, vertical section of Fig. 1. Here, as pre\iously, the composition at the FeO end of the diagram is nonstoichiometric, varying from Feo.950 when the liquid oxide is in contact with the solid iron, to about Fe 0, when the solid oxide is in equilibrium with an atmosphere of equal proportions of CO and C02 at the solidus temperature. The Fe/O ratio will be maintained in wustite in the presence of SiO,. However, the FeM/Fe++ ratio in the liquid will be lower because of the effect OIF the SiO, on the activity of the FeO. With the addition of MgO to wustite, the over-all composition (IvZg, Fe)@, has a value of x lying between 0.9 and 1.0 when the COz/CO ratio is 1.0&apos;. b) Microstructures. In general, published attention to refractory microstructures has been directed toward the phase analyses that accompany compositional variations. This is illustrated by Harvey6 in his work on silica brick and by wells7 in his work on periclase brick. In each case, a series of altered zones is encountered which provides a sequence of phase associations. If due consideration is given to reaction kinetics, such an examination reveals phases that are compatible with equilibrium studies. Admittedly, however, it is often necessary to determine more complicated polycomponent systems to account for all the phases present.8 Relatively little attention has been given to microstructural geometry in ceramic materials. Certainly less attention has been given to this aspect of ceramic microstructures than to the size, shape, and distribution of the constituent phases in metals. Burke has pointed out that the grain size of oxides follows the same growth rules as for metals, viz.,