Kinetics Of The Transfer Of Sulphur Across A Slag-Metal Interface

INTRODUCTION THE kinetics and mechanism of transfer of a constituent across a slag-metal interface are fundamentally important because many metallurgical processes involve the existence of a slag phase and a metal phase. Industrial processes seldom proceed to equilibrium, and information of the rates and modes of reactions are therefore often of greater practical importance than equilibrium data. A study of the kinetics of sulphur transfer across a slag-metal interface under reducing conditions will contribute a great deal toward a better understanding of desulphurization in the blast furnace process. The general principles existing in the transfer of a constituent, such as sulphur, across a slag-metal interface can be extended to similar transfer phenomena in other metallurgical processes. The present paper will demonstrate how such studies will lead to fruitful results from both the practical and theoretical standpoints. EXPERIMENTAL METHOD The apparatus used was simple. A graphite crucible 1 5/8-in. id, a wall 1/8-in. thick, and a depth of 4 in., was packed in an outer fused silica tube with powdered magnesia. The crucible assembly was rotated at a speed of 235 rpm inside an induction coil. A charge of 250 g of Armco ingot iron was introduced into the graphite crucible and melted by induction heating. The melt was held at a desired temperature [ ] for 3-5 min., after which 7.5 g of granular ferrous sulphide was added and the bath was held for another 3-5 min. A metal sample was then taken by means of a fused silica tube and a rubber suction bulb. Immediately after the metal sample was taken, 30 g of a prefused and crushed slag were introduced. The slag reached the temperature of the furnace in 1 to 1 1/ 2 min. Slag