Leaching of Lead from Solder Material used in Electrical and Electronic Equipment

Present work is a part of developing novel recycling technique for waste printed circuit boards (PCBs) i.e. the liberation of metals from PCBs by organic swelling followed by the treatment of resin to remove/ recover hazardous soldering materials. In order to recover the hazardous metallic constituent lead from the liberated resin, initially the leaching studies were made using fresh solder containing 63.9% Pb and remaining tin. Experimental results obtained in different conditions viz. time, temperature and acidity showed -97.20% of lead dissolution with 6M HNO3 at solid to liquid (S:L) ratio 1:10 (g/mL) and temperature 90°C in 75 minutes. The result of the studies validated with crushed PCBs shows that almost total lead and tin was leached out with 6M HNO3 and 6M HC1 respectively at S:L ratio 1:10 (g/mL) and temperature 90°C within 50 minutes. The results will be useful for the treatment and safe disposal of PCBs resin.