Low temperature pressure oxidation of copper gold-bearing flotation concentrate

"Test work was carried out using copper gold-bearing flotation concentrate with 6.85%Cu, 14.30%Fe, 20.70%S and 2.34%As. Gold and silver grade in the concentrate is 54.6 g/t and 92 g/t, respectively. Gold and copper are valuable components in the concentrate. Gold is partially associated with pyrite and fahlores. Copper in the concentrate can be found as tennantite (Cu12As4S13). The 71% of gold from the flotation concentrate is recoverable by cyanidation with simultaneous cyanide consumption in the amount of 96 kg/t. The major reason of refractoriness is that gold is fine encapsulated into sulfides and the presence of cyanicide-copper. The concentrate ground as much as 95% minus 10 µm was treated using low-temperature POX at the temperature of 100±5°C, L:S ratio of 5:1 and the process time of 1-5 hours. Residual sulfide sulfur in the cake is 2.28% which is 89% sulfide oxidation. The highest copper recovery to POX solution is 91%. It was found that gold recovery to cyanide solution is 85-94% during alkaline pre-treatment of POX cakes followed by cyanidation. In this case, cyanide and lime consumption is 75-90 kg/t and 120 kg/t, respectively. In order to recover precious metals from POX cakes leaching using sodium sulfite was carried out. Test work was conducted at varied reagent concentration, L:S ratio and leaching time. Gold and silver recovery achieved was 85-95% and 59-63%, respectively."