Mg-A1-(Sr, Ca) Systems - An Experimental Analysis

The phase equilibria in the Mg-Al-Ca system was investigated experimentally by differential scanning calorimetry (DSC) and X-ray diffraction (XRD) techniques similarly the Mg-Al-Sr system has been studied using DSC and XRD as well as scanning electron microscopy/energy dispersive spectrometer (SEM/EDS) and quantitative electron probe micro-analysis (EPMA). A new ternary solid solution MgxAl4,xSr was confirmed in Mg-Al-Sr system, which is a substitutional solid solution of Mg atoms in Al4Sr. Maximum solubilities of 21.3 at.% Al in Mg17Sr2 and 11.4 at.% Al in Mg were observed. It was also noticed that Mg38Sr9 dissolved 12.5 at.% Al. In the Mg-Al-Ca ternary system, one of the invariant transformations predicted by thermodynamic modeling was verified experimentally and found to occur at 512°C with composition close to 10.8 at.% Ca, 79.5 at.% Mg and 9.7 at.% Al. A ternary solid solution (Mg,Al)2Ca was confirmed where large solid solubility of Al in Mg2Ca was observed.