New York Paper - The Effect of Carbon on the Physical Properties of Heat-Treated Carbon Steel (with Discussion)

The experiments herein described were undertaken with a view to investigating thoroughly the influence of carbon on the tensile and impact physical properties of carbon steel. The original comprehensive plan included investigation of a series of steels with varying carbon contents over a wide range of heat treatments. These were to be studied as to their static tensile qualities, and also their resistance to shock as measured by the Charpy impact bending test. A thorough metallographic examination was likewise included in the schedule. The Charpy tests and the metallographic examination have not been completed to date, and are accordingly withheld for another report. All heat treatments, however, have been made, and the static tensile tests have been completed. A description of the procedure of the experiment and the results thus far obtained are therefore reported herein. Conclusions No attempt is made to draw general conclusions from these experiments, but the curves and the data are submitted as being of general importance and wide applicability. Composition of Materials An attempt was made to secure steels increasing in carbon by increments of 0.1 per cent. from 0.1 per cent. up to 0.8 per cent., and from that composition to 1.6 per cent. by increments of 0.2 per cent. Actually, however, steels of the composition given in Table I were procured, and as the carbon contents were arranged sufficiently well so that satisfactory curves could be drawn showing the relation between carbon content and other properties, these steels were used in the experiments.