Ni-YSZ cermet substrate supported thin SDC and YSZ+SDC bi-layer SOFCs

SOFCs with thin electrolyte of two types: SDC (15um) single-layer and YSZ (5um) + SDC (15um) bi-layer were fabricated by screen printing and co-firing on Ni¬YSZ cermet substrates. Using in-situ sintered Sm0.5Sr0.5CoO3 cathode the SDC-cell shows high performance at low temperature, 1180mW/cm2 peak power density around 650°C, while the YSZ+SDC bi-layer cell generates about 340mW/cm2 at 650°C, and good performance at 700-800°C with almost theoretical OCV value. Many Zr-content micro-islands were found on the SDC electrolyte surface. The influence of co-firing temperature and thin film preparation methods on the Zr-islands' appearance was investigated.